Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KetaSpire KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpire PEEK provides the maximum levels of mechanical properties at temperatures approaching 300°C and the lowest coefficient of linear thermal expansion within the KetaSpire product family. KetaSpire PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Filler Content 30 %
30 %
Carbon Fiber Reinforcement
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Viscosity 450000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
450000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm

@Thickness 3.18 mm
0.00 - 0.0020 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse 0.014 - 0.016 cm/cm

@Thickness 3.18 mm
0.014 - 0.016 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 400 °C
11 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 106
106
M-Scale; ASTM D785
Tensile Strength 223 MPa
32300 psi
ASTM D638
Tensile Strength, Yield 218 MPa
31600 psi
ISO 527-2/1A/5
Elongation at Break 1.7 %
1.7 %
5.0 mm/min; ASTM D638
1.7 %
1.7 %
ISO 527-2/1A/5
Tensile Modulus 20.9 GPa
3030 ksi
ASTM D638
25.4 GPa
3680 ksi
ISO 527-2/1A/1
Flexural Strength 319 MPa
46300 psi
ISO 178
321 MPa
46600 psi
ASTM D790
Flexural Modulus 17.9 GPa
2600 ksi
ASTM D790
21.5 GPa
3120 ksi
ISO 178
Compressive Strength 188 MPa
27300 psi
ASTM D695
Shear Strength 103 MPa
14900 psi
ASTM D732
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
6.40 J/cm
12.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 43.0 kJ/m²
20.5 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 6.70 µm/m-°C

@Temperature -50.0 - 50.0 °C
3.72 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
Specific Heat Capacity 1.31 J/g-°C

@Temperature 50.0 °C
0.313 BTU/lb-°F

@Temperature 122 °F
DSC
1.81 J/g-°C

@Temperature 200 °C
0.433 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.370 W/m-K
2.57 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 343 °C
649 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 315 °C
599 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 147 °C
297 °F
ASTM D3418
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 365 °C
689 °F
Middle Barrel Temperature 370 °C
698 °F
Front Barrel Temperature 375 °C
707 °F
Nozzle Temperature 380 °C
716 °F
Mold Temperature 175 - 205 °C
347 - 401 °F
Drying Temperature 150 °C
302 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Autoclave Sterilizable
E-beam Sterilizable
Ethylene Oxide Sterilizable
Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Sterilizability
Heat Sterilizable
High Flow
High Heat Resistance
High Stiffness
High Strength
Radiation (Gamma) Resistant
Radiation Sterilizable
Radiotranslucent
Steam Resistant
Steam Sterilizable
Forms Pellets
Generic PEEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
Screw Compression Ratio 2.5:1.0 to 3.5:1.0
Uses Aircraft Applications
Connectors
Dental Applications
Electrical/Electronic Applications
Film
Hospital Goods
Industrial Applications
Medical Appliances
Medical/Healthcare Applications
Oil/Gas Applications
Pump Parts
Seals
Surgical Instruments
Copyright © lookpolymers.com All Rights Reserved