Solvay TECHNYL® A 402H1 Natural PA66, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 402H1 Natural PA66, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 402H1 is an unreinforced polyamide 66, very high viscosity, heat stabilized, for extrusion and injection molding. This product is available in natural color.Benefits: The product offers three main advantages: high impact resistance at low humidity levels, good rigidity, and excellent compression resistance.Available in: Asia Pacific, Europe and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This grade is particularly suitable for the extrusion of window profiles or semi-finished products, and for the injection molding of plastic insulators for railway binding.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Water Absorption 1.5 %

@Temperature 23.0 °C,
Time 86400 sec
1.5 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527 Type 1A
Tensile Stress 30.0 MPa

@Strain 1.00 %
4350 psi

@Strain 1.00 %
55.0 MPa

@Strain 2.00 %
7980 psi

@Strain 2.00 %
70.0 MPa

@Strain 3.00 %
10200 psi

@Strain 3.00 %
78.0 MPa

@Strain 4.00 %
11300 psi

@Strain 4.00 %
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527 type 1 A
Elongation at Break 60 %
60 %
ISO 527 Type 1A
Elongation at Yield 8.0 %
8.0 %
ISO 527 type 1 A
Tensile Modulus 3.10 GPa
450 ksi
ISO 527 Type 1A
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75/Af
Oxygen Index 27 %
27 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 27.0 kV/mm
686 kV/in
IEC 60243
Dissipation Factor 0.020
0.020
IEC 60250
Comparative Tracking Index 475 V
475 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Die Temperature 280 - 290 °C
536 - 554 °F
Drying Temperature 80.0 °C

@Time 28800 sec
176 °F

@Time 8.00 hour
dew point -35°C
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C