Solvay TECHNYL® C 548B V15 Black PA6, 15% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 548B V15 Black PA6, 15% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced with 15% of glass fiber, heat stabilized, height viscosity, for extrusion-blowing.Available in: Asia Pacific and North AmericaProduct Applications: TECHNYL C 548B V15 is suitable in the automotive industry for blow-molded parts, mainly in the oil and air circuits, such as: air intake ducts, turbo to intercooler pipe, intercooler exit duct. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183/A |
| Water Absorption | 1.42 % @Temperature 23.0 °C, Time 86400 sec |
1.42 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 Type 1A |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
22.2 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 210 - 230 °C | 410 - 446 °F | |
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM100LN Polypropylene, Impact Copolymer, Medium Impact, Nucleated, Antistat, Injection Molding
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 18% Plasticizer (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66 (Asia Pacific)
- Sumitomo Bakelite Sumikon® PM-9501 Glass-Filled Phenolic, Compression Grade
- Solvay RHODACAL® 60/B Surfactant
- A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer
- Colorite Polymers CS9039GP Wire and Cable Insulation Vinyl Compound
- ATI Allvac® 35N Nickel Superalloy, Heat Treatment: 1052°C (1925°F) + Age
- Ashley Polymers Ashlene® R3137 BK PC/PBT
Copyright © lookpolymers.com All Rights Reserved