Material Notes:
Data provided by the manufacturer. Formulated to meet smoke and fire specifications recommended by the FTA, this is ideally suited for mass transit applications such as seat backs, overhead storage bins, trays, side panels and window surrounds.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ASTM D792
Water Absorption 0.010 %
0.010 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM D955
Melt Flow 3.9 g/10 min

@Load 5.00 kg,
Temperature 200 °C
3.9 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Condition G; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 99
99
ASTM D785
Tensile Strength, Yield 39.0 MPa
5660 psi
ASTM D638
Modulus of Elasticity 2.10 GPa
305 ksi
ASTM D638
Flexural Yield Strength 63.0 MPa
9140 psi
ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
ASTM D790
Izod Impact, Notched 1.50 J/cm
2.81 ft-lb/in
ASTM D256
0.400 J/cm

@Temperature -20.0 °C
0.749 ft-lb/in

@Temperature -4.00 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 135 µm/m-°C

@Temperature 20.0 °C
75.0 µin/in-°F

@Temperature 68.0 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Annealed; ASTM D648
Vicat Softening Point 79.0 °C
174 °F
ASTM D1525
Flammability, UL94 V-0
V-0
0.031 in. UL 94
Oxygen Index 43.2 %
43.2 %
ASTM D2863