Styron CALIBREâ„¢ 5201-8 Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 5201-8 Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: CALIBREâ„¢ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-8 resin is typically used in electrical market applications. CALIBRE 5201-8 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics: Glass reinforcedIgnition resistantISO 10993 Applications:Electrical boxesLighting componentsElectrical connectorsMedical applicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183/B; ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ISO 294-4; ASTM D955
Melt Flow 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength at Break 82.7 MPa
12000 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 82.7 MPa
12000 psi
50 mm/min; ISO 527-2/50; ASTM D638
Elongation at Break 3.0 %
3.0 %
50 mm/min; ASTM D638
Elongation at Yield 2.6 %
2.6 %
50 mm/min; ISO 527-2/50; ASTM D638
Tensile Modulus 5.17 GPa
750 ksi
50 mm/min; ISO 527-2/50; ASTM D638
Flexural Strength 148 MPa
21500 psi
Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Flexural Modulus 4.82 GPa
699 ksi
3-point; ISO 178
4.83 GPa
701 ksi
Method I (3 point load), 2.0 mm/min; ASTM D790
Izod Impact, Notched 1.10 J/cm

@Temperature 23.0 °C
2.06 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Dart Drop, Total Energy 46.3 J
34.1 ft-lb
3.39 m/sec; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 148 °C
298 °F
Annealed; ASTM D648
148 °C
298 °F
Annealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Unannealed; ISO 75-2/B; ASTM D648
142 °C
288 °F
Annealed; ISO 75-2/B; ASTM D648
Vicat Softening Point 158 °C
316 °F
ISO 306/B50
159 °C

@Load 5.10 kg
318 °F

@Load 11.2 lb
Rate A (50°C/h); ASTM D1525
Flammability, UL94 V-2

@Thickness 1.59 mm
V-2

@Thickness 0.0626 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in