TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Fastener Stock

Category Metal , Nonferrous Metal , Titanium Alloy , Alpha/Beta Titanium Alloy
Manufacturer TIMET
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Fastener Stock.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of fastener stock; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aerospace: AMS 4911, 4928, 4932, 4935, 4954, 4965, 4967. Germany Engineering: 3.7165. Germany Aerospace: 3.7164. France: T-A6V. UK Aerospace Specifications BS TA. 10,11, 12, 13, 28, 56 DTD 5363.Features: A versatile medium strength alloy, the "workhorse" TIMETAL 6-4 exhibits good tensile properties at room temperature, creep resistance up to 325°C and excellent fatigue strength. It is often used in less critical applications up to 400°C. TIMETAL 6-4 is the alloy most commonly used in wrought and cast forms. Palladium or ruthenium can be added for increased corrosion resistance. Most properties are affected by the microstructure, which is determined by the thermomechanical history. It is highly resistant to general corrosion in sea water. This alloy is available in most common product forms including billet, bar, wire, plate, and sheet.Data provided by TIMET.
Physical Properties Metric English Comments
Density 4.42 g/cc
0.160 lb/in³
Typical
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1205 MPa
174800 psi
Typical
Tensile Strength, Yield 1075 MPa

@Strain 0.200 %
155900 psi

@Strain 0.200 %
Typical
Elongation at Break 14 %
14 %
Typical
Modulus of Elasticity 105 - 120 GPa
15200 - 17400 ksi
Typical
Poissons Ratio 0.31
0.31
Shear Modulus 41.0 - 45.0 GPa
5950 - 6530 ksi
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C

@Temperature 0.000 - 100 °C
5.00 µin/in-°F

@Temperature 32.0 - 212 °F
9.40 µm/m-°C

@Temperature 20.0 - 425 °C
5.22 µin/in-°F

@Temperature 68.0 - 797 °F
9.70 µm/m-°C

@Temperature 20.0 - 650 °C
5.39 µin/in-°F

@Temperature 68.0 - 1200 °F
Specific Heat Capacity 0.586 J/g-°C
0.140 BTU/lb-°F
Thermal Conductivity 6.60 W/m-K
45.8 BTU-in/hr-ft²-°F
Melting Point 1674 °C
3045 °F
Liquidus >= 1636 °C
>= 2977 °F
Maximum Service Temperature, Air 350 °C
662 °F
Reasonable mechanical properties retained
Beta Transus 995 °C
1820 °F
Component Elements Properties Metric English Comments
Aluminum, Al 5.5 - 6.75 %
5.5 - 6.75 %
Carbon, C <= 0.080 %
<= 0.080 %
Hydrogen, H <= 0.015 %
<= 0.015 %
Iron, Fe <= 0.40 %
<= 0.40 %
Nitrogen, N <= 0.050 %
<= 0.050 %
Oxygen, O <= 0.20 %
<= 0.20 %
Titanium, Ti 87.6 - 91 %
87.6 - 91 %
Calculated as remainder
Vanadium, V 3.5 - 4.5 %
3.5 - 4.5 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000168 ohm-cm
0.000168 ohm-cm
Magnetic Permeability 1.00005
1.00005
at 20 oersteds