Wellman Wellamid® T423-BK10 Mineral Reinforced Nylon 6, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Wellman Engineering Resins
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wellman Wellamid® T423-BK10 Mineral Reinforced Nylon 6, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive cooling fans & shrouds, automotive door handles, brackets, automotive mirror shells, painted parts, components for small gas engines, sporting goods, auto luggage rack components.Data provided by the manufacturer, Wellman Inc.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Water Absorption 1.0 %
1.0 %
Approximate 24 hr.
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Flexural Yield Strength 125 MPa
18100 psi
ISO 178
Flexural Modulus 6.30 GPa
914 ksi
ISO 178
Izod Impact, Notched 0.300 J/cm
0.562 ft-lb/in
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
From Wellman QC Laboratory Testing; UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 277 - 293 °C
530 - 560 °F
Middle Barrel Temperature 271 - 288 °C
520 - 550 °F
Front Barrel Temperature 266 - 282 °C
510 - 540 °F
Nozzle Temperature 254 - 293 °C
490 - 560 °F
Melt Temperature 271 - 293 °C
520 - 560 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 79.4 °C
175 °F
Opened bags and gaylord boxes
Dry Time 2 - 4 hour
2 - 4 hour
Opened bags and gaylord boxes
Moisture Content 0.050 - 0.20 %
0.050 - 0.20 %
During molding to prevent hydrolytic degradation
<= 0.20 %
<= 0.20 %
In shipping bags, ready to mold
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Back Pressure 0.345 MPa
50.0 psi
Screw Speed 30 - 120 rpm
30 - 120 rpm