Zell-Metall Engineering Plastics Zellamid 1500T (PEEK modified)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer Zell-Metall Engineering Plastics
Trade Name Zellamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zell-Metall Engineering Plastics Zellamid 1500T (PEEK modified).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zellamid® 1500 (Polyetheretherketone - PEEK, natural) is the registered trademark for Zell-Metall’s semi-crystalline high performance thermoplastic which exhibits a unique combination of high mechanical properties, temperature resistance and excellent chemical resistance, making it the most popular advanced plastics material.Fields: Nuclear and Vacuum Technology, Aerospace Industry, Mechanical and Automotive Engineering, Conveyer Technology, Semiconductor Production, Electrical and Electronics, Wire and Cable, Oil Exploration, Chemical Processing Industry.Besides of the standard grade for tribological applications also our Zellamid® 1500 T grade is available in black color, modified with 10% Carbonfibre, 10% PTFE and 10% Graphite.Zellamid® 1500 T has an outstanding wear resistance and an even lower coefficient of friction as well as higher Pressure-Velocity capabilities.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 141 MPa
20500 psi
ISO 527; DIN 53455
Elongation at Break 2.0 %
2.0 %
ISO 527; DIN 53455
Tensile Modulus 9.00 GPa
1310 ksi
ISO 527; DIN 53452
Thermal Properties Metric English Comments
CTE, linear 22.0 µm/m-°C

@Temperature 20.0 °C
12.2 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
DIN 53612 Method A
Melting Point 340 °C
644 °F
ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air 260 °C
500 °F
5000 hours; 50% Tensile Strength; IEC 216; DIN 53446
300 °C
572 °F
a few hours operation
Deflection Temperature at 1.8 MPa (264 psi) 293 °C
559 °F
ISO 75; DIN 53461
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in