- Zyvex Performance Materials Arovex™ 180 Carbon Nanotube Strengthened Prepreg
Zyvex Performance Materials Arovex™ 180 Carbon Nanotube Strengthened Prepreg
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite |
| Manufacturer | Zyvex Performance Materials (ZPM) |
| Trade Name | Arovex™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zyvex Performance Materials Arovex™ 180 Carbon Nanotube Strengthened Prepreg.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Arovex® 180 Prepreg is a 180°F (82°C) curing carbon nanotube strengthened epoxy prepreg suitable for numerous composites applications. Arovex 180 resin contains an optimum level of carbon nanotubes for additional toughness and enhanced mechanical properties. The carbon nanotubes use molecular dispersion technology to ensure enhancements are evenly distributed throughout the resin. Features: Very high toughnessHigh strengthHigh stiffnessEnhanced mechanical properties Excellent retention of tack and drape
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 0.060 cP @Temperature 120 °C |
0.060 cP @Temperature 248 °F |
Rheology, 2°C/min |
| 0.070 cP @Temperature 80.0 °C |
0.070 cP @Temperature 176 °F |
Rheology, 2°C/min | |
| 0.75 cP @Temperature 40.0 °C |
0.75 cP @Temperature 104 °F |
Rheology, 2°C/min | |
| 100 cP @Temperature 140 °C |
100 cP @Temperature 284 °F |
Rheology, 2°C/min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 1790 MPa | 259000 psi | 0°; ASTM D3039 |
| Tensile Modulus | 132 GPa | 19200 ksi | 0°; ASTM D3039 |
| Flexural Strength | 68.3 MPa | 9900 psi | 90°; ASTM D790 |
| 1390 MPa | 201000 psi | 0°; ASTM D790 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | 90°; ASTM D790 |
| 113 GPa | 16400 ksi | 0°; ASTM D790 | |
| Compressive Strength | 1210 MPa | 175000 psi | 0°; SACMA SRM 1R-94 |
| Compressive Modulus | 128 GPa | 18500 ksi | 0°; SACMA SRM 1R-94 |
| Poissons Ratio | 0.32 | 0.32 | ASTM D3039 |
| Shear Strength | 79.3 MPa | 11500 psi | Short Beam; ASTM D5528-07 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 120 °C | 248 °F | ASTM D7028-07 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 600 min @Temperature 82.2 °C |
10.0 hour @Temperature 180 °F |
|
| Shelf Life | 12.0 Month @Temperature -17.8 °C |
12.0 Month @Temperature 0.000 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| GIc Strain Release Energy | 3.0 in-lb/in² | ASTM D5528-07 |