- Polymer Property : Melt Flow = 18 g/10 min
Polymer Property : Melt Flow = 18 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 8.0 - 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 - 18 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Polymer Resources PC/ASA-GP2 Polycarbonate/ASA Alloy Acrylonitrile Styrene Acrylate + PolycarbonatePreliminary DataProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.In.. |
|||
| Melt Flow | 3.0 - 18 g/10 min @Load 6.70 kg, Temperature 337 °C |
3.0 - 18 g/10 min @Load 14.8 lb, Temperature 639 °F |
ASTM D1238 |
| Polymer Resources PEI-G40 Polyetherimide, 40% Glass Reinforced Polyetherimide, 40% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly.. |
|||
| Melt Flow | 12 - 18 g/10 min @Load 11.6 kg, Temperature 250 °C |
12 - 18 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP3 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Injection MoldingNotes: All physical, mechanical and thermal testing.. |
|||
| Melt Flow | 12 - 18 g/10 min @Load 11.6 kg, Temperature 250 °C |
12 - 18 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP3-[color]-EN Modified-PPO, Extrusion Grade Modified-Polyphenylene Oxide, Extrusion Grade, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: ExtrusionNotes: All physical, mechanical and thermal testing conduct.. |
|||
| Melt Flow | 12 - 18 g/10 min @Load 11.6 kg, Temperature 250 °C |
12 - 18 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP3-IM Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 235F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 10 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 - 18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-FR2 Polybutylene Terephthalate, Flame Retardant Polybutylene Terephthalate, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided.. |
|||
| Melt Flow | 10 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 - 18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-FR2-[color]-WR Polybutylene Terephthalate, Flame Retardant, Wear Resistant Polybutylene Terephthalate, Flame Retardant, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Melt Flow | 5.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 - 18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-IM-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Impact Modified Polybutylene Terephthalate, 30% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Melt Flow | 8.0 - 18 g/10 min | 8.0 - 18 g/10 min | ASTM D1238 |
| Polymer Resources TPSF-FR1 PBT, 30% Glass Reinforced Structural Foam Grade, Flame Retardant Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
| Melt Flow | 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TPSF-FRG10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced, Flame Retardant Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced, Flame RetardantProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, .. |
|||
| Melt Flow | 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 18 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced Polybutylene Terephthalate, Structural Foam, 10% Glass ReinforcedProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Info.. |
|||
| Melt Flow | 8.0 - 18 g/10 min | 8.0 - 18 g/10 min | ASTM D1238 |
| Polymer Resources TPSF-GP1 PBT, 30% Glass Reinforced Structural Foam Grade Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
| Melt Flow | 12 - 18 g/10 min | 12 - 18 g/10 min | ASTM D1238 |
| Polymer Resources PPX-GP3 Modified PPO, General Purpose with HDT of 235 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 12 - 18 g/10 min | 12 - 18 g/10 min | ASTM D1238-92 |
| Iran Petrochemical (PCC) Tabriz 3630/1 High Impact Polystyrene
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
| Melt Flow | 14 - 18 g/10 min @Load 2.16 kg, Temperature 190 °C |
14 - 18 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| FKuR Kunststoff Bio-Flex® F 6513 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
| Melt Flow | 12.1 - 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
12.1 - 18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Iran Petrochemical (PCC) PC 1218 Polycarbonate Suitable for molding, injection, and blow moldingInformation provided by Iran Petrochemical Commercial Co. |
|||
| Melt Flow | 8.0 - 18 g/10 min @Load 5.00 kg, Temperature 372 °C |
8.0 - 18 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
| Solvay Specialty Polymers Hyflon® MFA® F1540 Perfluoropolymer Hyflon® MFA is a unique family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame re.. |
|||
| Melt Flow | 15 - 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 - 18 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Samyang Triel® 5400 Thermoplastic Polyether Ester Elastomer TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor r.. |
|||
| Melt Flow | 15 - 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 - 18 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Samyang Triel® 5407EF Thermoplastic Polyether Ester Elastomer TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor r.. |
|||
| Melt Flow | 8.0 - 18 g/10 min @Load 2.16 kg, Temperature 224 °C |
8.0 - 18 g/10 min @Load 4.76 lb, Temperature 435 °F |
ASTM D1238 |
| Lubrizol Pellethane® 2363-55D Thermoplastic Polyurethane Elastomer Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009. |
|||
| Melt Flow | 14 - 18 g/10 min @Load 2.16 kg, Temperature 190 °C |
14 - 18 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D 1238 |
| Cossa Polimeri ESTALENE EN 25 C Modified Polyolefin Blend Formulated for injection molding or extrusion of synthetic corksCertified according to FDA standardsInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 9.0 - 18 g/10 min @Load 5.00 kg, Temperature 372 °C |
9.0 - 18 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
| Daikin NEOFLON AP-210 PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Injection molded parts, wire insulation, etc.Information provided .. |
|||
| Melt Flow | 9.0 - 18 g/10 min @Load 5.00 kg, Temperature 372 °C |
9.0 - 18 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
| Daikin NEOFLON EP-620 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl.. |
|||
| Melt Flow | 10 - 18 g/10 min | 10 - 18 g/10 min | ASTM D1238 |
| Buckeye Polymers BP FLEX D4107 GO1 BLK Thermoplastic Polyolefin Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist.. |
|||
| Melt Flow | 4.0 - 18 g/10 min @Load 12.5 kg, Temperature 232 °C |
4.0 - 18 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR FLEX® 2850 Black Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
| Melt Flow | 7.0 - 18 g/10 min | 7.0 - 18 g/10 min | |
| Asahi Glass Fluon® P-63P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Melt Flow | 7.0 - 18 g/10 min | 7.0 - 18 g/10 min | |
| Asahi Glass Fluon® P-810UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Melt Flow | 15 - 18 g/10 min @Load 2.16 kg, Temperature 235 °C |
15 - 18 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Gromax PBT 1100-211MB Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
| Melt Flow | 10 - 18 g/10 min | 10 - 18 g/10 min | ASTM D1238 |
| Buckeye Polymers BP RPP 4010 TU NAT Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||