Ascend Performance Materials Vydyne® R860 BK02 Nylon 66, Glass/Mineral Reinforced, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Ascend Performance Materials (formerly Solutia) |
| Trade Name | VYDYNE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ascend Performance Materials Vydyne® R860 BK02 Nylon 66, Glass/Mineral Reinforced, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vydyne® R860 BK02 is general-purpose, glass-fiber and mineral-reinforced PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Glass fiber and mineral-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Typical Applications/End Uses: Vydyne R860 BK02 can be successfully used in a wide range of injection-molding engineering applications. Typical parts include automotive clips, radiator shrouds, fans and mirror brackets; electrical connectors, housings and bobbins; and industrial applications such as gears, bearing shells, covers and housings. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass FiberMineral Additive:Lubricant Features: Good Mold Releasehigh RigidityHigh Strength High Tensile Strength LubricatedOutstanding Surface Finish Uses:Automotive Under the HoodGearsHousingsLawn and Garden EquipmentMetal ReplacementPower/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % @Time 86400 sec |
0.60 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Diameter 2.00 mm |
0.0025 in/in @Diameter 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Diameter 2.00 mm |
0.0080 in/in @Diameter 0.0787 in |
ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-2 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527-2 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Poissons Ratio | 0.40 | 0.40 | ISO 527-2 |
| Izod Impact, Notched (ISO) | 4.60 kJ/m² @Temperature -30.0 °C |
2.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 5.60 kJ/m² @Temperature 23.0 °C |
2.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 4.30 J/cm² @Temperature -30.0 °C |
20.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 4.80 J/cm² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.380 J/cm² @Temperature -30.0 °C |
1.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.440 J/cm² @Temperature 23.0 °C |
2.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
13.3 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
38.3 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Melting Point | 255 °C | 491 °F | ISO 11357-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 310 °C | 536 - 590 °F | |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | |
| Front Barrel Temperature | 280 - 310 °C | 536 - 590 °F | |
| Nozzle Temperature | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Max Regrind | 25 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY6010 PC+ABS (Europe-Africa-Middle East)
- Pyrotek TS-117 Thermoset Electrical Insulation Product (Nema Grade: GPO-1)
- SABIC Innovative Plastics Lexan® FXG1414T PC Copolymer (Europe-Africa-Middle East)
- LG Chemical LUPOY HR5007A PC/ABS, Heat Resistance, High Impact
- Lanxess Pocan® B 3215 XF 000000 PBT, 10% Glass Fiber
- Lucent Polymers TPP-240 Polypropylene, 40% Talc Filled, Impact Modified
- Lehmann & Voss LUVOCOM® 1106-8374 Polyether imide, with carbon fiber and PTFE
- Covestro Bayflex® 110-50 Polyurethane
- Colorite Polymers CS1534SR Wire and Cable Insulation Vinyl Compound
- Arlon 51580R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved