Clariant Renol PCSP0015 Polycarbonate, Carbon Fiber Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PCSP0015 Polycarbonate, Carbon Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 135 - 152 °C | 275 - 305 °F | |
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
| Dry Time | 2 - 4 hour @Temperature 48.9 °C |
2 - 4 hour @Temperature 120 °F |
to eliminate surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled
- Karina Karintox 70/2 Polyolefin Compound
- Lanxess Pocan® DP 2004 000000 PBT
- Haysite SDL® H400 Polyester Composite
- Johnson Matthey Matti-sil 30 Cadmium Free Brazing Alloy
- Techmer ES HiFill® PA6/6 LGF60 HS L BK 12 mm
- A. Schulman POLYFORT™ FPP 3707 CAC03 Filled Homopolymer Polypropylene
- ChevronTexaco ISO 68 Utility Oil HVI
- BNZ Materials CS85 High Temperature Structural Insulation
- Alpase M-5™ Aluminum Mold Plate
Copyright © lookpolymers.com All Rights Reserved