DuPont Performance Polymers Crastin® S600F10 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® S600F10 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection Molding Crastin S600F10 NC010 is an unreinforced lubricated medium high viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.50 %
<br>@Thickness 2.00 mm
 0.50 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %
<br>@Thickness 2.00 mm
 0.200 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 116000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 260 °C
 116000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
148000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 250 °C
 148000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
194000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 194000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
279000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 260 °C
 279000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
369000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 250 °C
 369000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
496000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 496000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 10.1 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 10.1 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 5.910 MPa
<br>@Strain 3.58031 %,<br> Temperature 150 °C
 857.1 psi
<br>@Strain 3.58031 %,<br> Temperature 302 °F
 ISO 11403-1 -2
10.46 MPa
<br>@Strain 2.84 %,<br> Temperature 90.0 °C
 1517 psi
<br>@Strain 2.84 %,<br> Temperature 194 °F
 ISO 11403-1 -2
12.81 MPa
<br>@Strain 14.3213 %,<br> Temperature 150 °C
 1858 psi
<br>@Strain 14.3213 %,<br> Temperature 302 °F
 ISO 11403-1 -2
14.44 MPa
<br>@Strain 25.0622 %,<br> Temperature 150 °C
 2095 psi
<br>@Strain 25.0622 %,<br> Temperature 302 °F
 ISO 11403-1 -2
19.98 MPa
<br>@Strain 1.85 %,<br> Temperature 40.0 °C
 2898 psi
<br>@Strain 1.85 %,<br> Temperature 104 °F
 ISO 11403-1 -2
20.87 MPa
<br>@Strain 9.55 %,<br> Temperature 90.0 °C
 3027 psi
<br>@Strain 9.55 %,<br> Temperature 194 °F
 ISO 11403-1 -2
23.459 MPa
<br>@Strain 0.768184 %,<br> Temperature -40.0 °C
 3402.4 psi
<br>@Strain 0.768184 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
23.89 MPa
<br>@Strain 16.78 %,<br> Temperature 90.0 °C
 3465 psi
<br>@Strain 16.78 %,<br> Temperature 194 °F
 ISO 11403-1 -2
24.579 MPa
<br>@Strain 0.8588 %,<br> Temperature 0.000 °C
 3564.9 psi
<br>@Strain 0.8588 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
24.63 MPa
<br>@Strain 23.49 %,<br> Temperature 90.0 °C
 3572 psi
<br>@Strain 23.49 %,<br> Temperature 194 °F
 ISO 11403-1 -2
31.6 MPa
<br>@Strain 1.33 %,<br> Temperature 23.0 °C
 4580 psi
<br>@Strain 1.33 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
35.26 MPa
<br>@Strain 7.41 %,<br> Temperature 40.0 °C
 5114 psi
<br>@Strain 7.41 %,<br> Temperature 104 °F
 ISO 11403-1 -2
39.33 MPa
<br>@Strain 12.94 %,<br> Temperature 40.0 °C
 5704 psi
<br>@Strain 12.94 %,<br> Temperature 104 °F
 ISO 11403-1 -2
40.12 MPa
<br>@Strain 18.47 %,<br> Temperature 40.0 °C
 5819 psi
<br>@Strain 18.47 %,<br> Temperature 104 °F
 ISO 11403-1 -2
49.3 MPa
<br>@Strain 2.28 %,<br> Temperature 23.0 °C
 7150 psi
<br>@Strain 2.28 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
54.0 MPa
<br>@Strain 3.23 %,<br> Temperature 23.0 °C
 7830 psi
<br>@Strain 3.23 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
54.50 MPa
<br>@Strain 2.147 %,<br> Temperature 0.000 °C
 7905 psi
<br>@Strain 2.147 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
69.28 MPa
<br>@Strain 3.4352 %,<br> Temperature 0.000 °C
 10050 psi
<br>@Strain 3.4352 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
74.71 MPa
<br>@Strain 3.07274 %,<br> Temperature -40.0 °C
 10840 psi
<br>@Strain 3.07274 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
93.67 MPa
<br>@Strain 5.37729 %,<br> Temperature -40.0 °C
 13590 psi
<br>@Strain 5.37729 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
5.00 MPa
<br>@Strain 0.280 %,<br> Time 3.60e+6 sec
 725 psi
<br>@Strain 0.280 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
5.00 MPa
<br>@Strain 0.220 %,<br> Time 360000 sec
 725 psi
<br>@Strain 0.220 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
5.00 MPa
<br>@Strain 0.195 %,<br> Time 3600 sec
 725 psi
<br>@Strain 0.195 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
5.00 MPa
<br>@Strain 0.202 %,<br> Time 36000 sec
 725 psi
<br>@Strain 0.202 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
5.00 MPa
<br>@Strain 0.397 %,<br> Time 3.60e+7 sec
 725 psi
<br>@Strain 0.397 %,<br> Time 10000 hour
 isochronous; ISO 11403-1 -2
20.0 MPa
<br>@Strain 0.820 %,<br> Time 3600 sec
 2900 psi
<br>@Strain 0.820 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
20.0 MPa
<br>@Strain 2.61 %,<br> Time 3.60e+7 sec
 2900 psi
<br>@Strain 2.61 %,<br> Time 10000 hour
 isochronous; ISO 11403-1 -2
25.0 MPa
<br>@Strain 1.17 %,<br> Time 36000 sec
 3630 psi
<br>@Strain 1.17 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
25.0 MPa
<br>@Strain 1.34 %,<br> Time 360000 sec
 3630 psi
<br>@Strain 1.34 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
25.0 MPa
<br>@Strain 2.03 %,<br> Time 3.60e+6 sec
 3630 psi
<br>@Strain 2.03 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
Tensile Strength, Yield 57.0 MPa
8270 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Flexural Strength 85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
Shear Modulus 0.0640 GPa
<br>@Temperature 160 °C
 9.28 ksi
<br>@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.0900 GPa
<br>@Temperature 120 °C
 13.1 ksi
<br>@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.187 GPa
<br>@Temperature 70.0 °C
 27.1 ksi
<br>@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
0.869 GPa
<br>@Temperature 20.0 °C
 126 ksi
<br>@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
0.959 GPa
<br>@Temperature -20.0 °C
 139 ksi
<br>@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.07 GPa
<br>@Temperature -50.0 °C
 155 ksi
<br>@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.094872 GPa
<br>@Strain 22.0028 %,<br> Temperature 100 °C
 13.760 ksi
<br>@Strain 22.0028 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.164 GPa
<br>@Strain 11.0014 %,<br> Temperature 100 °C
 23.8 ksi
<br>@Strain 11.0014 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.270 GPa
<br>@Strain 14.77 %,<br> Temperature 40.0 °C
 39.1 ksi
<br>@Strain 14.77 %,<br> Temperature 104 °F
 ISO 11403-1 -2
0.30625 GPa
<br>@Strain 2.72 %,<br> Temperature 100 °C
 44.418 ksi
<br>@Strain 2.72 %,<br> Temperature 212 °F
 ISO 11403-1 -2
0.476 GPa
<br>@Strain 7.41 %,<br> Temperature 40.0 °C
 69.0 ksi
<br>@Strain 7.41 %,<br> Temperature 104 °F
 ISO 11403-1 -2
1.08 GPa
<br>@Strain 1.85 %,<br> Temperature 40.0 °C
 157 ksi
<br>@Strain 1.85 %,<br> Temperature 104 °F
 ISO 11403-1 -2
1.55 GPa
<br>@Strain 6.14547 %,<br> Temperature -40.0 °C
 225 ksi
<br>@Strain 6.14547 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
1.82 GPa
<br>@Strain 3.8646 %,<br> Temperature 0.000 °C
 265 ksi
<br>@Strain 3.8646 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
2.16 GPa
<br>@Strain 2.28 %,<br> Temperature 23.0 °C
 314 ksi
<br>@Strain 2.28 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
2.38 GPa
<br>@Strain 1.33 %,<br> Temperature 23.0 °C
 345 ksi
<br>@Strain 1.33 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2