DuPont Performance Polymers Rynite® RE5264 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Rynite® RE5264 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
36% Glass Reinforced Polyethylene Terephthalate Rynite RE5264 NC010 is a 36% glass fiber reinforced color stabilized modified polyethylene terephthalate.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 16 g/10 min
<br>@Load 5.00 kg,<br> Temperature 280 °C
 16 g/10 min
<br>@Load 11.0 lb,<br> Temperature 536 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
ISO 527-1/-2
Tensile Stress 34.16 MPa
<br>@Strain 1.05 %,<br> Temperature 150 °C
 4954 psi
<br>@Strain 1.05 %,<br> Temperature 302 °F
 ISO 11403-1 -2
48.51 MPa
<br>@Strain 0.370 %,<br> Temperature 40.0 °C
 7036 psi
<br>@Strain 0.370 %,<br> Temperature 104 °F
 ISO 11403-1 -2
49.38 MPa
<br>@Strain 0.340 %,<br> Temperature -20.0 °C
 7162 psi
<br>@Strain 0.340 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
50.61 MPa
<br>@Strain 0.890 %,<br> Temperature 90.0 °C
 7340 psi
<br>@Strain 0.890 %,<br> Temperature 194 °F
 ISO 11403-1 -2
53.04 MPa
<br>@Strain 2.61 %,<br> Temperature 150 °C
 7693 psi
<br>@Strain 2.61 %,<br> Temperature 302 °F
 ISO 11403-1 -2
58.39 MPa
<br>@Strain 3.39 %,<br> Temperature 150 °C
 8469 psi
<br>@Strain 3.39 %,<br> Temperature 302 °F
 ISO 11403-1 -2
61.19 MPa
<br>@Strain 0.450 %,<br> Temperature 23.0 °C
 8875 psi
<br>@Strain 0.450 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
62.37 MPa
<br>@Strain 0.450 %,<br> Temperature 0.000 °C
 9046 psi
<br>@Strain 0.450 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
63.54 MPa
<br>@Strain 4.42 %,<br> Temperature 150 °C
 9216 psi
<br>@Strain 4.42 %,<br> Temperature 302 °F
 ISO 11403-1 -2
82.28 MPa
<br>@Strain 2.21 %,<br> Temperature 90.0 °C
 11930 psi
<br>@Strain 2.21 %,<br> Temperature 194 °F
 ISO 11403-1 -2
89.69 MPa
<br>@Strain 2.87 %,<br> Temperature 90.0 °C
 13010 psi
<br>@Strain 2.87 %,<br> Temperature 194 °F
 ISO 11403-1 -2
94.15 MPa
<br>@Strain 3.53 %,<br> Temperature 90.0 °C
 13660 psi
<br>@Strain 3.53 %,<br> Temperature 194 °F
 ISO 11403-1 -2
113.15 MPa
<br>@Strain 0.880 %,<br> Temperature 23.0 °C
 16411 psi
<br>@Strain 0.880 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
118.7 MPa
<br>@Strain 1.02 %,<br> Temperature 40.0 °C
 17220 psi
<br>@Strain 1.02 %,<br> Temperature 104 °F
 ISO 11403-1 -2
126.69 MPa
<br>@Strain 0.970 %,<br> Temperature 0.000 °C
 18375 psi
<br>@Strain 0.970 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
134.68 MPa
<br>@Strain 1.01 %,<br> Temperature -20.0 °C
 19534 psi
<br>@Strain 1.01 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
140.18 MPa
<br>@Strain 1.30 %,<br> Temperature 40.0 °C
 20331 psi
<br>@Strain 1.30 %,<br> Temperature 104 °F
 ISO 11403-1 -2
154.42 MPa
<br>@Strain 1.33 %,<br> Temperature 23.0 °C
 22397 psi
<br>@Strain 1.33 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
156.11 MPa
<br>@Strain 1.57 %,<br> Temperature 40.0 °C
 22642 psi
<br>@Strain 1.57 %,<br> Temperature 104 °F
 ISO 11403-1 -2
161.35 MPa
<br>@Strain 1.33 %,<br> Temperature 0.000 °C
 23402 psi
<br>@Strain 1.33 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
176.9 MPa
<br>@Strain 1.43 %,<br> Temperature -20.0 °C
 25660 psi
<br>@Strain 1.43 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
178.06 MPa
<br>@Strain 1.68 %,<br> Temperature 23.0 °C
 25825 psi
<br>@Strain 1.68 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
182.46 MPa
<br>@Strain 1.59 %,<br> Temperature 0.000 °C
 26464 psi
<br>@Strain 1.59 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
198.28 MPa
<br>@Strain 1.68 %,<br> Temperature -20.0 °C
 28758 psi
<br>@Strain 1.68 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 2.4 %
2.4 %
ISO 527-1/-2
Tensile Modulus 14.0 GPa
2030 ksi
ISO 527-1/-2
Shear Modulus 0.558 GPa
<br>@Temperature 170 °C
 80.9 ksi
<br>@Temperature 338 °F
 Dynamic; ISO 11403-1 -2
0.626 GPa
<br>@Temperature 130 °C
 90.8 ksi
<br>@Temperature 266 °F
 Dynamic; ISO 11403-1 -2
1.892 GPa
<br>@Temperature 70.0 °C
 274.4 ksi
<br>@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
2.408 GPa
<br>@Temperature 20.0 °C
 349.3 ksi
<br>@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
2.483 GPa
<br>@Temperature -20.0 °C
 360.1 ksi
<br>@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
2.604 GPa
<br>@Temperature -50.0 °C
 377.7 ksi
<br>@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 8.25 GPa
<br>@Strain 2.12 %,<br> Temperature 40.0 °C
 1200 ksi
<br>@Strain 2.12 %,<br> Temperature 104 °F
 ISO 11403-1 -2
9.10 GPa
<br>@Strain 2.20 %,<br> Temperature 23.0 °C
 1320 ksi
<br>@Strain 2.20 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
9.34 GPa
<br>@Strain 1.76 %,<br> Temperature 40.0 °C
 1350 ksi
<br>@Strain 1.76 %,<br> Temperature 104 °F
 ISO 11403-1 -2
10.1 GPa
<br>@Strain 1.86 %,<br> Temperature 23.0 °C
 1460 ksi
<br>@Strain 1.86 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
10.5 GPa
<br>@Strain 1.39 %,<br> Temperature 40.0 °C
 1520 ksi
<br>@Strain 1.39 %,<br> Temperature 104 °F
 ISO 11403-1 -2
10.7 GPa
<br>@Strain 1.94 %,<br> Temperature 0.000 °C
 1540 ksi
<br>@Strain 1.94 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
11.4 GPa
<br>@Strain 1.85 %,<br> Temperature -20.0 °C
 1650 ksi
<br>@Strain 1.85 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
11.4 GPa
<br>@Strain 1.41 %,<br> Temperature 23.0 °C
 1650 ksi
<br>@Strain 1.41 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
11.6 GPa
<br>@Strain 1.02 %,<br> Temperature 40.0 °C
 1690 ksi
<br>@Strain 1.02 %,<br> Temperature 104 °F
 ISO 11403-1 -2
11.9 GPa
<br>@Strain 1.41 %,<br> Temperature 0.000 °C
 1730 ksi
<br>@Strain 1.41 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
12.2 GPa
<br>@Strain 1.52 %,<br> Temperature -20.0 °C
 1770 ksi
<br>@Strain 1.52 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
12.858 GPa
<br>@Strain 0.880 %,<br> Temperature 23.0 °C
 1864.9 ksi
<br>@Strain 0.880 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
13.1 GPa
<br>@Strain 0.970 %,<br> Temperature 0.000 °C
 1890 ksi
<br>@Strain 0.970 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
13.1 GPa
<br>@Strain 0.370 %,<br> Temperature 40.0 °C
 1900 ksi
<br>@Strain 0.370 %,<br> Temperature 104 °F
 ISO 11403-1 -2
13.3 GPa
<br>@Strain 1.01 %,<br> Temperature -20.0 °C
 1930 ksi
<br>@Strain 1.01 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
13.6 GPa
<br>@Strain 0.450 %,<br> Temperature 23.0 °C
 1970 ksi
<br>@Strain 0.450 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
13.86 GPa
<br>@Strain 0.450 %,<br> Temperature 0.000 °C
 2010 ksi
<br>@Strain 0.450 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
14.5 GPa
<br>@Strain 0.340 %,<br> Temperature -20.0 °C
 2110 ksi
<br>@Strain 0.340 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 246 °C
475 °F
10°C/min; ISO 11357-1/-3
Electrical Properties Metric English Comments
Dielectric Strength 21.5 kV/mm
546 kV/in
IEC 60243-1
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved