Eastman Eastar GN007 PETG Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , PETG Copolyester |
| Manufacturer | Eastman Chemical |
| Trade Name | Eastar |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Eastar GN007 PETG Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 3.9 % | 3.9 % | |
| Tensile Modulus | 1.88 GPa | 273 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.960 J/cm² | 4.57 ft-lb/in² | |
| 0.370 J/cm² @Temperature -30.0 °C |
1.76 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature 20.0 °C |
52.2 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | |
| Vicat Softening Point | 76.0 °C | 169 °F | |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY6110 PC+ABS (Europe-Africa-Middle East)
- Chevron Phillips Ryton® PR39 Polyphenylene Sulfide Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7353/NAT Polyacetal-copolymer, with aramid reinforcement and PTFE
- Ineos L80Z-00 Impact Copolymer Polypropylene
- SABIC Innovative Plastics LNP THERMOCOMP RZ0069 PA 66 (Asia Pacific)
- Sawbones Laminated Test Blocks
- Formosa Plastics Formolene® 5101M Staple Fiber and Injection Molding Polypropylene
- American Elements Lanthanum Nanoparticles
- Carpenter Kovar® Alloy (Glass and Ceramic Sealing Alloy)
Copyright © lookpolymers.com All Rights Reserved