Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/CC/30 Polypropylene Homopolymer, 30% Calcium Carbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 6.35 mm |
0.011 in/in @Thickness 0.250 in |
ASTM D955 |
| 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 | |
| Melt Flow | 13 g/10 min | 13 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Yield | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | ASTM D638 |
| Flexural Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs B820 (NH4)2B4O7.4H2O Ammonium tetraborate tetrahydrate
- Polystrand ThermoPro™ IE7020X X-Ply Cross-Ply Polyethylene-Glass Composite
- SABIC Innovative Plastics LNP LUBRICOMP 9X06030 PA 46 (Europe-Africa-Middle East)
- LG Chemical LI968W Co-Extrusion ASA
- Lanxess Durethan® BKV 140 000000 Copolyamide, 40% Glass Fiber
- TIMET 6-6-2 Titanium Alloy (Ti-6Al-6V-2Sn), Annealed
- A. Schulman POLYBATCH™ 10178Z Amber Concentrate Based in LDPE
- Adell AT-34 Nylon 66, 20% Glass Reinforced; Impact Modified
- Bulk Molding Compounds BMC T12(18) General Purpose Molding Compound
- Alliance Polymers Zythane™ 7075A Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved