Lanxess Durethan® DP 1100/30 H2.0 901510 Nylon 6, Micro Glass Balls
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 1100/30 H2.0 901510 Nylon 6, Micro Glass Balls.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA6, molding grade, micro glass balls, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.351 g/cc | 0.04881 lb/in³ | ISO 1183 |
| Melt Flow | 115 g/10 min @Load 5.00 kg, Temperature 280 °C |
115 g/10 min @Load 11.0 lb, Temperature 536 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Conditioned; ISO 527-1/-2 |
| 75.0 MPa | 10900 psi | ISO 527-1/-2 | |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Conditioned; ISO 527-1/-2 |
| 80.0 MPa | 11600 psi | ISO 527-1/-2 | |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-1/-2 |
| 155 % | 155 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527-1/-2 |
| 15 % | 15 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.35 GPa | 196 ksi | Conditioned; ISO 527-1/-2 |
| 4.30 GPa | 624 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| >= 15.0 J/cm² @Temperature 23.0 °C |
>= 71.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-040,GB30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 KG20 Nylon 6 for injection molding, 20% chalk filled
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 7% Plasticizer (discontinued **)
- Ferro CF 7574 Glaze and Sealant Glass
- Schwartz Technical Plastics MITELA® HD8B Cotton Fabric, Special Quality
- Dow DOWLEX™ 2503.10 Linear Low Density Polyethylene, Narrow MW Distribution
- Colorite Polymers 8087 General Purpose Vinyl Compound
- 3M Scotch-Weld™ 1838 B/A Tan Two-Part Structural Adhesive
- Resistalloy International Fecralloy™ 134 Electrical Resistance Steel
Copyright © lookpolymers.com All Rights Reserved