- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Polyram RamShine PV300G4 ABS, 20% Glass Fiber
Polyram RamShine PV300G4 ABS, 20% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PV300G4 ABS, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass fiber reinforced, heat resistant and minimal mold shrinkage ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | DIN 53479 |
| Water Absorption | 0.14 % | 0.14 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Melt Flow | 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM-D785 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM-D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM-D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM-D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
Users viewing this material also viewed the following:
- MV Labs LA100 La(C2H3O2)3·xH2O Lanthanum acetate hydrate
- ND Industries StudGrade® 131 Permanent CT Threadlocker
- Heatbath/Park Nu-Sal High Speed Hardening Salt
- Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion
- Daikin POLYFLON MG-6030 PTFE 15% Carbon Fiber Filled Molding Powder
- 3A Composites Core Materials AIREX® PXc.320 Fiber-Reinforced Structural Foam
- Formosa Plastics Formolene® LH5212 Injection Molding HDPE (discontinued **)
- PolyOne Edgetek® PI-10GF/000 Polyetherimide (PEI), Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved