- SABIC Innovative Plastics LNP THERMOCOMP RC006XXH PA 66
SABIC Innovative Plastics LNP THERMOCOMP RC006XXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC006XXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RC006XXH is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.274 g/cc | 0.04603 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 267 MPa | 38700 psi | 5 mm/min; ISO 527 |
| 269 MPa | 39000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 24.76 GPa | 3591 ksi | 1 mm/min; ISO 527 |
| 25.2 GPa | 3650 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 364 MPa | 52800 psi | ISO 178 |
| 382 MPa | 55400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 18.96 GPa | 2750 ksi | 2 mm/min; ISO 178 |
| 20.3 GPa | 2940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.02 J/cm | 1.91 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.8 J/cm | 20.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 262 °C @Thickness 3.20 mm |
504 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 281-73MED Thermoplastic Elastomer (discontinued **)
- PolyOne Stat-Tech™ NN-20CF/000 Black Polyamide 66 (Nylon 66)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR MBT
- Lucite International Diakon® ST50G8 Toughened Acrylic Polymer
- Solvay Specialty Polymers Halar® 7114 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East)
- Teknor Apex Sinpolene TPP1040 Polypropylene
- CP-Polymer-Technik Wellamid® 6000 HWV0CP Nylon 6, Flame Protection, Heat Stabilized, Dry
- Aclo Accutech Polypropylene Copolymer CP0436G10M20CL Glass/Mineral Reinforced Coupled
- BASF Ultradur B 4040 G3 HT BK5830 15% Glass Filled PBT/PET
Copyright © lookpolymers.com All Rights Reserved