Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 15% of glass fiber, for injection molding, heat stabilized, with improved hydrolysis resistance.Available in: North AmericaProduct Applications: TECHNYL ® a 218W V15 is used in all sectors of industry, offering an excellent combination of thermal and mechanical properties. This grade is recommended for the production of mechanical components in permanent or intermittent contact with hot water: e.g. electro-magnetic valves. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0073 cm/cm | 0.0073 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 Type 1A |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 Type 1A |
| Tensile Modulus | 6.07 GPa | 880 ksi | ISO 527 Type 1A |
| Flexural Modulus | 5.27 GPa | 764 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S KA 40A-3S1767 Thermoplastic Elastomer (TPE)
- Proto3000 Objet Digital Materials™ DM_9120/9420/9220/9320 Rubber-like Prototyping Polymer
- NOVA Chemicals Novapol® TE-0546-GBK Hexene MDPE Extrusion Resin
- Quadrant EPP Duratron® PI D7000 PI Unfilled Polyimide (ASTM Product Data Sheet)
- Huntsman PE1020 Film Extrusion Polyethylene (discontinued **)
- Hexcel® HexForce™ GA090 Carbon Fabric
- Denka VINYKON R5205 PVC, R grade for hard extrusion
- Bulk Molding Compounds tetra-DUR F 4209 Bulk Molding Compound
- 3M 7120 Performance Paper Label Material
- SABIC Innovative Plastics Lexan® 950A PC
Copyright © lookpolymers.com All Rights Reserved