- Styron Pulse® 1350 ABS + Polycarbonate
Styron Pulse® 1350 ABS + Polycarbonate
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Styron Pulse® 1350 ABS + Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSE® 1350 Engineering resin offers a superior total performance with a balance of heat resistance, practical toughness, high and low temperature impact strength retention and ease of processing.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM Data |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Melt Flow | 3.0 g/10 min <br>@Load 3.80 kg,<br> Temperature 230 °C |
3.0 g/10 min <br>@Load 8.38 lb,<br> Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM Data |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM Data |
| Elongation at Break | 100 % | 100 % | ASTM Data |
| Elongation at Yield | 4.2 % | 4.2 % | ISO Data |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO Data. |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM Data |
| 2.67 J/cm <br>@Temperature -50.0 °C |
5.00 ft-lb/in <br>@Temperature -58.0 °F |
ASTM Data | |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO Data, Low Temp |
| 5.60 J/cm² | 26.7 ft-lb/in² | ISO Data | |
| Impact Test | 56.5 J <br>@Temperature -30.0 °C |
41.7 ft-lb <br>@Temperature -22.0 °F |
Instrumented Dart Total Energy |
| 56.5 J <br>@Temperature 23.0 °C |
41.7 ft-lb <br>@Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C <br>@Temperature 20.0 °C |
41.0 µin/in-°F <br>@Temperature 68.0 °F |
ASTM data |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ASTM Data |
| 121 °C | 250 °F | annealed; ASTM Data | |
| Vicat Softening Point | 139 °C | 282 °F | |
| Flammability, UL94 | HB <br>@Thickness 1.47 mm |
HB <br>@Thickness 0.0579 in |
Users viewing this material also viewed the following:
- Precision Polymer Engineering C70H Chloroprene Rubber
- Chevron Phillips 5102 LDPE Injection Blow Molding Resin (discontinued **)
- SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East)
- Solvay Specialty Polymers Tecnoflon® FOR 210 Fluoroelastomer
- TIMET 6-6-2 Titanium Alloy (Ti-6Al-6V-2Sn), Annealed
- Ensinger HYDLAR® Z Nylon, Pultruded Aramid Fiber Reinforced (PA)
- Diamond Polymers ABS/PC 9901
- Braskem TS7010 LDPE Blown Film Extrusion Polyethylene
- Arlon LW201R##-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)
- Arlon 51808R011 0.011" (0.279 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved