Sumitomo Bakelite North America E 264H Long Glass Fiber Reinforced Epoxy
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America E 264H Long Glass Fiber Reinforced Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
E 264H is a high strength, long fiberglass reinforced epoxy molding compound, which features improved flow in transfer molding.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.250 g/cc | 0.00903 lb/in³ | ASTM D1895 |
| Density | 1.82 g/cc | 0.0658 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Temperature 50.0 °C, Time 173000 sec |
0.15 % @Temperature 122 °F, Time 48.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 105 | 105 | ASTM D2583 |
| Tensile Strength at Break | 94.0 MPa | 13600 psi | ASTM D638 |
| Flexural Strength | 235 MPa | 34100 psi | at rupture; ASTM D790 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ASTM D790 |
| Compressive Strength | 203 MPa | 29400 psi | ASTM D695 |
| Izod Impact, Notched | 7.28 J/cm | 13.6 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | As Molded; ASTM D648A |
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |
| Shrinkage | 0.090 % | 0.090 % | Post Shrinkage; ASTM D955 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Frequency 60.0 Hz |
381 kV/in @Frequency 60.0 Hz |
step-by-step, wet; ASTM D149 |
| 15.4 kV/mm @Frequency 60.0 Hz |
391 kV/in @Frequency 60.0 Hz |
step-by-step, dry; ASTM D149 | |
| 17.0 kV/mm @Frequency 60.0 Hz |
432 kV/in @Frequency 60.0 Hz |
short time, wet; ASTM D149 | |
| 17.4 kV/mm @Frequency 60.0 Hz |
442 kV/in @Frequency 60.0 Hz |
short time, dry; ASTM D149 | |
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Form | Coarse Flake | |
| Molding Method | Compression | |
| Transfer |