Toyobo GLAMIDE® T-403 Nylon-6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-403 Nylon-6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-403 is a GF reinforced Nylon-6. It contains 45% GF.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 45 % | 45 % | |
| Water Absorption | 1.1 % | 1.1 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0030 - 0.0060 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0060 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 90.0 MPa @Temperature 80.0 °C |
13100 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 |
| 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 200 MPa @Temperature 23.0 °C |
29000 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| 290 MPa @Temperature -40.0 °C |
42100 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.2 % | 3.2 % | Absolute Drying; ASTM-D638 |
| 3.4 % | 3.4 % | Practical Use (Water Absorption 2.0%); ASTM-D638 | |
| Flexural Strength | 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 150 MPa @Temperature 80.0 °C |
21800 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 290 MPa @Temperature 23.0 °C |
42100 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 300 MPa @Temperature -40.0 °C |
43500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 360 MPa @Temperature -40.0 °C |
52200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 4.50 GPa @Temperature 80.0 °C |
653 ksi @Temperature 176 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 |
| 6.80 GPa @Temperature 80.0 °C |
986 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 7.20 GPa @Temperature 23.0 °C |
1040 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 12.0 GPa @Temperature 23.0 °C |
1740 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 12.5 GPa @Temperature -40.0 °C |
1810 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D790 | |
| 13.9 GPa @Temperature -40.0 °C |
2020 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 160 MPa | 23200 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 1.15 J/cm @Temperature -40.0 °C |
2.15 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.40 J/cm @Temperature -40.0 °C |
2.62 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 | |
| 1.90 J/cm @Temperature 23.0 °C |
3.56 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 2.50 J/cm @Temperature 23.0 °C |
4.68 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 2.0%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 2.0%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 4.2 @Frequency 1000 Hz |
4.2 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 2.00 mm |
483 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 2.0%); ASTM-D149 |
| 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Arc Resistance | 92 sec | 92 sec | Practical Use (Water Absorption 2.0%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 550 V | 550 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 75.0 - 95.0 MPa | 10900 - 13800 psi |
Users viewing this material also viewed the following:
- Ovation Polymers RIGITRON 30530 GF Polyester, 30% Glass Reinforced
- PolyOne Maxxam™ 34-1520 SSM TFPP Polypropylene Homopolymer (PP Homopolymer)
- Gromax BFG30-B103N1 Nylon 6 33% Glass Filled (Conditioned)
- KKPC Kuhmo HF401 Flame Retarded General Purpose HIPS
- H.C. Starck Amperit® 553.065 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- A. Schulman PP 1579 Polypropylene Impact Grade Polypropylene
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- Dow TUFLIN™ HSE-1003 NT 7 Linear Low Density Polyethylene Resin
- Bohler-Uddeholm UDDEHOLM ORVAR® SUPERIOR (Premium AISI H13) Hot Work Tool Steel
Copyright © lookpolymers.com All Rights Reserved