Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 63 µm | 63 µm | Mean |
Potters Industries Q-Cel® 5032S Hollow Engineered Glass Microspheres Q-CEL® hollow glass microspheres are alternatives to conventional fillers and additives such as silicas, calcium carbonates, talc, clay, etc. A variety of particle sizes, densities and strengths me.. |
|||
Particle Size | 63 µm | 63 µm | Mean |
Potters Industries Q-Cel® 7036 Hollow Engineered Glass Microspheres Q-CEL® hollow glass microspheres are alternatives to conventional fillers and additives such as silicas, calcium carbonates, talc, clay, etc. A variety of particle sizes, densities and strengths me.. |
|||
Particle Size | <= 63 µm | <= 63 µm | 1.80% retained; ISO 1624 |
SABIC PVC 673E Emulsion Polyvinyl Chloride Product Description: PVC 673E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi.. |
|||
Particle Size | <= 63 µm | <= 63 µm | 1% retained; ISO 1624 |
SABIC PVC 703E Emulsion Polyvinyl Chloride for Paste Preparation Product Description: PVC 703E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi.. |
|||
Particle Size | <= 63 µm | <= 63 µm | 0.75% retained; ISO 1624 |
SABIC PVC 741E Emulsion Polyvinyl Chloride for Paste Preparation Product Description: PVC 741E is a fine particle, high molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting low viscositie.. |
|||
Particle Size | 63 µm | 63 µm | 15% max, wet sieve |
Magyar Aluminum ALO-DFM Alumina Alumina for Polishing |
|||
Particle Size | 63 µm | 63 µm | 3% max, wet sieve |
Magyar Aluminum ALO-DN-7P Alumina Ground Alumina |
|||
Particle Size | 63 µm | 63 µm | 3% max, wet sieve |
Magyar Aluminum ALO-EL-7P Alumina Ground Alumina |
|||
Particle Size | 63 µm | 63 µm | Maximum of 5% greater than |
H.C. Starck Amperit® 526.077 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
Particle Size | 63 µm | 63 µm | Maximum 5% greater than, for WC-Co 83-17 |
H.C. Starck Amperit® 560.077 Tungsten Carbide-Cobalt(83-17)-Nickel-SF RC 60 50-50 (Wc-Co / NiSF RC 60) Composition is of NiSF RC 60 only |
|||
Particle Size | 63 µm | 63 µm | Maximum of 10% greater than |
H.C. Starck Amperit® 821.084 Zirconia-Yttria 80-20 (ZrO2-Y2O3) |
|||
Particle Size | <= 63 µm | <= 63 µm | >95% for PM |
H.C. Starck CuNi 97/3 Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | <= 63 µm | <= 63 µm | >95% for PM |
H.C. Starck FeNiCo Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | <= 63 µm | <= 63 µm | >95% for PM |
H.C. Starck NiAl 97/3 Atomized Powder Ni- and FE based alloys for special P/M, HIP and MIM parts, Cu based alloys for brazing. |
|||
Particle Size | 63 µm | 63 µm | >80% greater than value; ISO 1624 |
SolVin 250SB Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Injection : moldings with complex flow paths
Pressing : mixed with VC-VAc copolymers for gramophone records
Calendering : rigid films and sheets ; use.. |
|||
Particle Size | 63 µm | 63 µm | >97% greater than value; ISO 1624 |
SolVin 257RF Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Extrusion : unplasticized PVC
- profile
- foam
- sheet, film
- blow moldings
Calendering : unplasticized PVC
- film : high temperature process
Injecti.. |
|||
Particle Size | 63 µm | 63 µm | >90% greater than value; ISO 1624 |
SolVin 258RD Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Blow extrusion : opaque or crystal-clear bottles
Injection molding : rigid articles
Calendering : opaque or crystal-clear rigid sheets
Extrusion : rig.. |
|||
Particle Size | 63 µm | 63 µm | >95% greater than value; ISO 1624 |
SolVin 260RF Polyvinyl Chloride General Purpose - Rigid Made by suspension polymerization.
APPLICATIONS
Extrusion : unplasticized PVC
- tubes/pipes
- profile
- foam
- sheet, film
- blow moldings
Calendering : unplasticized PVC
- film : high temperature p.. |
|||
Particle Size | 63 µm | 63 µm | <0.5 g/kg greater than value; ISO 1624 |
SolVin 266SC Polyvinyl Chloride Pastes - filler Polymers Made by suspension polymerization.
APPLICATIONS
Filler polymer for plastisols.
CHARACTERISTICS
SolVin 266SC is a suspension resin with very low porosity, small particle size and a very low amount of.. |
|||
Particle Size | >= 63 µm | >= 63 µm | >95% retained on 63 micron sieve; ISO 1624 |
SolVin 267RC Polyvinyl Chloride Homopolymer Extrusion Grade Polyvinyl chloride made by suspension polymerization. Uses: Sewage pipes, pressure pipes, rigid profiles, window frames, electrical ductsInformation provided by SolVin. |
|||
Particle Size | 63 µm | 63 µm | >95% greater than value; ISO 1624 |
SolVin 271GA Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid pipes for medical applications
- plasticized film for blood bags
Injection molding : plasticized and semi-rig.. |
|||
Particle Size | 63 µm | 63 µm | >90% greater than value; ISO 1624 |
SolVin 271PC Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid profiles and pipes
- blowing of plasticized films
Calendering : opaque or transparent, plasticized and semi-r.. |
|||
Particle Size | 63 µm | 63 µm | >60% greater than value; ISO 1624 |
SolVin 560RA Copolymer of Vinyl Chloride and Vinyl Acetate Made by suspension polymerization.
APPLICATIONS
Extrusion : sheets for vacuum-forming, for deformations of over 500 %
Calendering : rigid sheets for deep thermoformingInformation provided by SolVin... |
|||
Particle Size | >= 63 µm | >= 63 µm | d50, 40%, Vibrated sieving |
TIMCAL TIMREX® KS150 Primary Synthetic Graphite TIMREX Primary Synthetic Graphite is produced in a unique highly controlled graphitization process which assures narrow specifications and unequalled consistent quality due to: monitoring of all pro.. |
|||
Particle Size | 63 µm | 63 µm | 10% below |
BorsodChem ONGROVIL S-468 Suspension PVC-Resin S-468 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It re.. |
|||
Particle Size | 63 µm | 63 µm | 5% below |
BorsodChem ONGROVIL S-5064 Suspension PVC-Resin S-5064 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It r.. |
|||
Particle Size | 63 µm | 63 µm | 5% below |
BorsodChem ONGROVIL S-5167 Suspension PVC-Resin S-5167 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It r.. |
|||
Particle Size | 63 µm | 63 µm | 10% below |
BorsodChem ONGROVIL S-465 Suspension PVC-Resin S-465 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It re.. |
|||
Particle Size | 63 µm | 63 µm | 5% below |
BorsodChem ONGROVIL S-5258 Suspension PVC-Resin S-5258 is a suspension type PVC homopolymer of medium molecular mass. It is characterized by a porous particle structure, a narrow range of particle size and a relatively high apparent density. It r.. |
|||
Particle Size | 63 µm | 63 µm | >90% greater than value; ISO 1624 |
SolVin 275SC Polyvinyl Chloride General Purpose - Plasticized Made by suspension polymerization.
APPLICATIONS
Extrusion :
- plasticized and semi-rigid profiles and pipes
Calendering : opaque or transparent, plasticized and semi-rigid films and sheets.Informati.. |