Polymer Property : Ball Indentation Hardness = 21800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	150 MPa	21800 psi	dry; ISO 2039-1
Murtfeldt Murylon® B Nylon 6 Murylon® B natural has the best impact resistance of all Murylon materials. This material is especially suited for use in machine construction thanks to an excellent combination of mechanical prope..
Ball Indentation Hardness	150 MPa	21800 psi	ISO2039.1 DIN.53456
Omnia Plastica Akulon® PA6 G.Oil Omniamid Oil - Dry Cast Nylon 6 with the addition of 6% of special lubricating oil which remains in solution in the material. The unique method of production results in a micro distribution of oil particles with a hom..
Ball Indentation Hardness	150 MPa	21800 psi	ISO2039.1 DIN.53456
Omnia Plastica Akulon® POM h Acetal Homopolymer The general features of homopolymer acetalic resin are similar to those of copolymer POM c, except that service temperature (under load) is slightly higher but resistance to hydrolysis and strong al..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL A63 GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL B63 KV20 Nylon 6 for injection molding, 20% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Quadrant EPP Ertalon® 6 SA PA 6, extruded (ISO Data) This material offers an optimal combination of mechanical strength, stiffness, toughness, mechanical damping properties and wear resistance. These properties, together with good electrical insulatin..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL A63 K Nylon 6.6 for injection molding Nylon 6.6 for injection molding, formulated for the coloration of button baths.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL B63 SG30 Nylon 6 for injection molding, 30% mineral filled Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL B63 W-KV20 Nylon 6 for injection molding, 20% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Nilit FRIANYL C73 MG40 Nylon 6.6/6 for injection molding, 40% mineral filled Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Lanxess DurethanÂ® B 40 SK 000000 Nylon 6 PA 6, non-reinforced, injection molding
Ball Indentation Hardness	150 MPa	21800 psi	H 358/30; Ã˜ 50x4mm; ISO 2039-1
SYNTHOS KrastenÂ® 152 General Purpose Polystyrene Improved heat resistance, very good rheological properties.Examples of Application:Injection moulding â€“ vegetable boxes for refrigerators, shower enclosure panels, CD and DVD cases. Blends with..
Ball Indentation Hardness	150 MPa	21800 psi	Hc 30; ISO 2039; partially
Schwartz Technical Plastics LAMIGAMIDÂ® 327 Cast Polyamide 6, MoS2, Heat Stabilized, Conditioned Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH
Ball Indentation Hardness	150 MPa @Load 36.5 kg, Time 30.0 sec	21800 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Styrolution Polystyrol 143 E GR 2 PS Description: Polystyrol 143 E is a medium strength, easy flowing general purpose grade, suitable for blending with impact modified Polystyrol, Styrolux and coextruded gloss layers.Applications: In b..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Styrolution PS 124 N/L GPPS Styrolution PS 124N/L is a general purpose polystyrene grade with a good flow characteristic and an improved heat resistance.Excellent flow propertiesHigh heat resistanceUL 94 HB (Antwerp only)Infor..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Styrolution PS 156F GPPS Styrolution PS 156F is a general purpose polystyrene grade with excellent flow properties, high heat resistance and is zinc stearate free.Free of internal lubricantsHigh heat resistanceExcellent flo..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Styrolution PS 165 N/L GPPS Styrolution PS 165N/L is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.High molecular weightGood flow characteristicsAppropriate for blending with HIPS..
Ball Indentation Hardness	150 MPa @Load 36.5 kg, Time 30.0 sec	21800 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Styrolution Polystyrol 165 H GR 21 PS Description: Polystyrol 165 H is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.Applications: In blends with high impact Polystyrene or Styrolux; thermo..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Styrolution PS 158 N/L GPPS Styrolution PS 158N/L is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact polystyrene in heat contact applications; for..
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
Styrolution PS 158K GPPS Styrolution PS 158K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact Styrolution PS in heat contact applications; fo..
Ball Indentation Hardness	150 MPa	21800 psi	H 358/30; ISO 2039; DIN 53456
Zell-Metall Engineering Plastics Zellamid 202 (PA 6) Zellamid® 202 is a tough material with high resistance to abrasion and impact. It features good mechanical properties. By water absorption the excellent shock and vibration resistance is increased...
Ball Indentation Hardness	150 MPa	21800 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno..
Ball Indentation Hardness	150 MPa	21800 psi	dry; ISO 2039-1
EMS-Grivory Grivory® XE 4185 black 9453 PA* Product description: Grivory XE 4185 is a non-reinforced heat stabilized engineering thermoplastic material based on a semicrystalline, partially aromatic copolyamide. ISO polymer designation: PA 10..
Ball Indentation Hardness	150 MPa	21800 psi	GB3398
Beijing Evergrow Resources Oilon Information provided by Beijing Evergrow Resources.
Ball Indentation Hardness	150 MPa	21800 psi	ISO 2039-1
BASF Ultradur® B 4300 K4 20% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 20% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit..
Ball Indentation Hardness	150 MPa	21800 psi	value at 30 sec.; ISO 2039-1
CENTROPLAST CENTROCARB GF Polycarbonate 30% glass fiber CENTROCARB GF is a transparent or semi-transparent plastic, reinforced for high strength and impact resistance. It has a high tensile modulus of elasticity and is well suited for structural element..
Ball Indentation Hardness	150 - 200 MPa	21800 - 29000 psi	Average value: 170 MPa Grade Count:4
Overview of materials for Polybutylene Terephthalate (PBT), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Bead Filled". Each property range of values reported is minimum ..