Polymer Property : Tensile Strength, Yield = 3630 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.0 MPa	3630 psi
Radici Radilon® A USZ200 (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength, Yield	25.0 MPa	3630 psi	50 mm/min; ISO 527
Phillips Sumika Marlex® CHN-200 Thermoplastic Polyolefin (discontinued **) Thermoplastic Polyolefin, High Stiffness, Talc-FilledApplications: Automotive InteriorsConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.9-1.1%Drying conditionsTemperature: 80-100°CTim..
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ASTM D638
Reliance Industries Repol B220MN Polypropylene REPOL Polypropylene B220MN is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Tensile Strength, Yield	25.0 - 90.0 MPa	3630 - 13100 psi	Average value: 63.5 MPa Grade Count:41
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb ..
Tensile Strength, Yield	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM D638
BASF Capron® 8200 NL Nylon 6 (DAM) (discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Tensile Strength, Yield	25.0 MPa	3630 psi
LyondellBasell LupolenÂ® 5236 HX HDPE, Impact Grade Medium flow, impact resistant, high stress-crack resistant grade for closures for bottles that contain carbonated liquids. This product contains a slip agent.Data was collected by ISO methods and o..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
Flint Hills AP5325-HS Impact Copolymer Polypropylene High impact copolymer, UL certified, and FDA compliant. Features: Nucleated and heat stabilizedApplications: Injection molding: large, thin wall automotive interior parts.Former Huntsman polypropyle..
Tensile Strength, Yield	25.0 MPa	3630 psi	50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 3-3120 B 20% Talc-Filled Polypropylene INNOPOLÂ® CS 3-3120 B is a black colored, 20% talc-filled polypropylene compound.INNOPOLÂ® CS 3-3120 B is a recommended for producing injection molded products where the required property is hig..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638-02
Ipiranga Petrochem PCC 4414 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D 638
LyondellBasell Hostacomâ„¢ BA742EC Polypropylene Copolymer Description: Hostacomâ„¢ BA742EC low melt flow, 1,200 MPa flexural modulus, precolored, extrusion grade polypropylene copolymer has a good balance of strength, stiffness, impact resistance and pr..
Tensile Strength, Yield	25.0 MPa	3630 psi	ISO 527
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
SPS Guang Zhou SAMATâ„¢ 168(f1) Flame-retarded Polypropylene Characteristic: Good flame resistance, good chemical resistance, good mechanical propertiesApplications: X'mas decorative product, E/E applianceInformation Provided by SPS (Guang Zhou) Ltd.
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
SPS Guang Zhou SAMATâ„¢ 5000A Flame-retarded Polypropylene Characteristic: Good flame retardance, non-halogen, high flow properties, high rigidity, high heat resistance, meets the requirements of RoHs and PaHsApplications: Lighting fitting, E/E applianceInf..
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ISO 527-2
Borealis BJ360MO Polypropylene Copolymer BJ360MO is a heterophasic copolymer. This grade provides unique combination of very high melt flow rate, high impact strength and stiffness. and is designed for high-speed injection molding and cont..
Tensile Strength, Yield	25.0 MPa	3630 psi	50mm/min; ISO 527-2
Borealis RA130E-6015 Polypropylene Random Copolymer RA130E-6015 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is green colored. Applications: domestic water, heating, relining, plumbing, and indust..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.0 MPa	3630 psi	50 mm/min; ASTM D638
A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene DescriptionPolypropylene PP 1407L-01 is a super high-impact copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.0 MPa	3630 psi	ISO 527-2
Total Polystyrene Impact 6540 Easy Flow Impact Polystyrene POLYSTYRENE IMPACT 6540 is an easy flowing, high impact polystyrene with a good balance of mechanical and thermal properties. This resin combines physical properties such as the flow necessary for ..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
Total PPC 4944CWZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 4944CWZ is a nucleated and controlled rheology impact copolymer with a very high Melt Flow index of 50 g/10 min.TOTAL 4944CWZ is characterized by improved stiffnes..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D 638
Cossa Polimeri ESTAPROP H 1080 T6 T D Polypropylene, 40% Mineral Filled PP homopolymer 40% mineral fillerGood physical and mechanical characteristics, high thermal stability, detergent resistanceInformation provided by Cossa Polimeri S.r.l.
Tensile Strength, Yield	25.0 MPa	3630 psi	50 mm/min; ISO 527
Eurostar Starpylen MB006SU PP, Glass Bead Filled, Injection Molding Resin Starpylen MB006SU is a Glass Bead Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
BASF Ultramid® 8202C HS PA6 (Conditioned) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Tensile Strength, Yield	25.0 MPa	3630 psi	50 mm/min
Arkema Group Rilsan® BMN P40 D Nylon 11 (Conditioned) Designation ISO 1874-PA11-P,MR,12-003Flexible grade for injection molding. Available colors: black, natural and white. Mold release agent.Flexibility. Outstanding working properties. Easy filling of..
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
Braskem CP 741 Extrusion Polypropylene Heterophasic Copolymer Sheet extrusion.Information provided by Braskem.
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436G5M25CL Glass/Mineral Reinforced Coupled
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D-638
Bapolene® 5010H High Density Polyethylene This resin is a high molecular weight, high density copolymer polyethylene resin. Product exhibits superior impact strength and ESCR. Resin contains a process stabilizer and complies with FDA 21 C..
Tensile Strength, Yield	25.0 MPa	3630 psi
Radici Radilon® A USX200 (cond.) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
Tensile Strength, Yield	25.0 MPa	3630 psi
Radici Radilon® S ESL128 (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638
A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329HU is a high flow UV stabilized, medium impact copolymer polypropylene. Information provided by A. Schulman.
Tensile Strength, Yield	25.0 MPa	3630 psi	ISO 527-2/50
ExxonMobil PP7064L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow, high stiffness and antistatic properties. It is suitable for molding applications like consumer products, closures, contain..