Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 75.0 - 85.0 MPa | 10900 - 12300 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Aquanyl Nylon 612 Copolymer Aquanyl is a copolymer of Nylon 6 and Nylon 12 produced via the anionic polymerization process using the monomer's Caprolactam and Laurinlactam. It has reduced water absorption, improved stability a.. |
|||
Tensile Strength, Yield | 79.0 - 85.0 MPa | 11500 - 12300 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Moly Cast Nylon 6, MoS2 Filled Nylacast Moly is part of the Cast Nylon 6 family. Its improved crystallization occurs by the addition of Molybdenum Disulphide. It includes MoS2, which is an extremely effective self dry lubricant w.. |
|||
Tensile Strength, Yield | 75.0 - 85.0 MPa | 10900 - 12300 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Nylube Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant) This supreme wear resistant grade contains a combined liquid/solid lubricant system, which allows for a coefficient of friction as low as 0.08. The material has outstanding Pressure-Velocity capabil.. |
|||
Tensile Strength, Yield | 55.0 - 85.0 MPa | 7980 - 12300 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIKES® (PA 6 G) Cast Polyamide POLIKES® PA6 G (CAST POLYAMIDE) is a plastic with high physical, electrical and chemical resistance. Its resistance is high especially against strokes and loads. Its temperature resistance is high.. |
|||
Tensile Strength, Yield | 55.0 - 85.0 MPa | 7980 - 12300 psi | ISO.527 DN.53455 |
Polimersan Plastics POLIKES® (PA 6 G) Cast Polyamide POLIKES® PA6 G (CAST POLYAMIDE) is a plastic with high physical, electrical and chemical resistance. Its resistance is high especially against strokes and loads. Its temperature resistance is high.. |
|||
Tensile Strength, Yield | 60.0 - 85.0 MPa | 8700 - 12300 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
Tensile Strength, Yield | 55.0 - 85.0 MPa | 7980 - 12300 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Tensile Strength, Yield | 25.0 - 85.0 MPa | 3630 - 12300 psi | Average value: 60.5 MPa Grade Count:51 |
Overview of materials for Acrylic, General Purpose, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, General Purpose, Molded". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Yield | 47.0 - 85.0 MPa | 6810 - 12300 psi | Average value: 66.8 MPa Grade Count:11 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Tensile Strength, Yield | 57.2 - 85.0 MPa | 8300 - 12300 psi | Average value: 68.7 MPa Grade Count:4 |
Overview of materials for Styrene/Methyl Methacrylate Copolymer (SMMA) This property data is a summary of similar materials in the MatWeb database for the category "Styrene/Methyl Methacrylate Copolymer (SMMA)". Each property range of values reported is minimum and max.. |