Overview of materials for Nylon 6, 20% Mineral Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 6, 20% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.05 - 1.66 g/cc
0.0379 - 0.0600 lb/in³
Average value: 1.28 g/cc Grade Count:27
Filler Content 20.0 - 23.0 %
20.0 - 23.0 %
Average value: 21.0 % Grade Count:3
Water Absorption 0.200 - 7.20 %
0.200 - 7.20 %
Average value: 1.21 % Grade Count:14
Moisture Absorption at Equilibrium 1.20 - 2.50 %
1.20 - 2.50 %
Average value: 1.83 % Grade Count:7
Linear Mold Shrinkage 0.00100 - 0.0150 cm/cm
0.00100 - 0.0150 in/in
Average value: 0.00884 cm/cm Grade Count:25
Linear Mold Shrinkage, Transverse 0.00750 - 0.0100 cm/cm
0.00750 - 0.0100 in/in
Average value: 0.00860 cm/cm Grade Count:4
Melt Flow 3.00 - 20.0 g/10 min
3.00 - 20.0 g/10 min
Average value: 8.50 g/10 min Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90.0 - 93.0
90.0 - 93.0
Average value: 91.5 Grade Count:4
Hardness, Rockwell R 110 - 121
110 - 121
Average value: 118 Grade Count:5
Tensile Strength, Ultimate 38.0 - 105 MPa
5510 - 15200 psi
Average value: 70.9 MPa Grade Count:17
24.0 - 65.0 MPa

@Temperature -40.0 - 80.0 °C
3480 - 9430 psi

@Temperature -40.0 - 176 °F
Average value: 44.5 MPa Grade Count:1
Tensile Strength, Yield 47.0 - 85.0 MPa
6810 - 12300 psi
Average value: 66.8 MPa Grade Count:11
Elongation at Break 1.50 - 50.0 %
1.50 - 50.0 %
Average value: 7.87 % Grade Count:22
Modulus of Elasticity 1.80 - 6.40 GPa
261 - 928 ksi
Average value: 5.16 GPa Grade Count:14
Flexural Yield Strength 63.0 - 145 MPa
9140 - 21000 psi
Average value: 107 MPa Grade Count:22
38.0 - 110 MPa

@Temperature -40.0 - 80.0 °C
5510 - 16000 psi

@Temperature -40.0 - 176 °F
Average value: 75.5 MPa Grade Count:1
Flexural Modulus 2.26 - 7.40 GPa
328 - 1070 ksi
Average value: 4.50 GPa Grade Count:21
1.20 - 7.20 GPa

@Temperature -40.0 - 80.0 °C
174 - 1040 ksi

@Temperature -40.0 - 176 °F
Average value: 4.55 GPa Grade Count:1
Izod Impact, Notched 0.340 - 1.90 J/cm
0.637 - 3.56 ft-lb/in
Average value: 0.600 J/cm Grade Count:14
0.300 - 0.450 J/cm

@Temperature -40.0 - -40.0 °C
0.562 - 0.843 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.375 J/cm Grade Count:1
Izod Impact, Notched (ISO) 3.00 - 5.00 kJ/m²
1.43 - 2.38 ft-lb/in²
Average value: 4.22 kJ/m² Grade Count:9
2.00 - 4.00 kJ/m²

@Temperature -40.0 - -20.0 °C
0.952 - 1.90 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.00 kJ/m² Grade Count:4
Izod Impact, Unnotched (ISO) 15.0 - 45.0 kJ/m²
7.14 - 21.4 ft-lb/in²
Average value: 27.0 kJ/m² Grade Count:5
Charpy Impact Unnotched 3.00 J/cm² - NB
14.3 ft-lb/in² - NB
Average value: 3.46 J/cm² Grade Count:7
1.00 - 2.50 J/cm²

@Temperature -30.0 - -20.0 °C
4.76 - 11.9 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 2.00 J/cm² Grade Count:4
Charpy Impact, Notched 0.200 - 2.00 J/cm²
0.952 - 9.52 ft-lb/in²
Average value: 0.650 J/cm² Grade Count:7
0.200 - 0.200 J/cm²

@Temperature -30.0 - -20.0 °C
0.952 - 0.952 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.200 J/cm² Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 42.0 - 100 µm/m-°C
23.3 - 55.6 µin/in-°F
Average value: 59.5 µm/m-°C Grade Count:9
CTE, linear, Transverse to Flow 70.0 - 94.0 µm/m-°C
38.9 - 52.2 µin/in-°F
Average value: 78.0 µm/m-°C Grade Count:3
Melting Point 215 - 223 °C
419 - 433 °F
Average value: 219 °C Grade Count:8
Deflection Temperature at 0.46 MPa (66 psi) 177 - 230 °C
350 - 446 °F
Average value: 204 °C Grade Count:17
Deflection Temperature at 1.8 MPa (264 psi) 70.0 - 200 °C
158 - 392 °F
Average value: 129 °C Grade Count:20
Vicat Softening Point 200 - 207 °C
392 - 405 °F
Average value: 203 °C Grade Count:6
UL RTI, Electrical 60.0 - 65.0 °C
140 - 149 °F
Average value: 62.5 °C Grade Count:8
UL RTI, Mechanical with Impact 60.0 - 65.0 °C
140 - 149 °F
Average value: 62.5 °C Grade Count:8
UL RTI, Mechanical without Impact 60.0 - 65.0 °C
140 - 149 °F
Average value: 62.5 °C Grade Count:8
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:26
Glow Wire Test 650 - 960 °C
1200 - 1760 °F
Average value: 871 °C Grade Count:8
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+8 - 1.00e+15 ohm-cm
1.00e+8 - 1.00e+15 ohm-cm
Average value: 7.50e+14 ohm-cm Grade Count:11
Surface Resistance 1.00e+10 - 1.00e+15 ohm
1.00e+10 - 1.00e+15 ohm
Average value: 3.35e+14 ohm Grade Count:6
Dielectric Constant 3.30 - 6.00
3.30 - 6.00
Average value: 4.26 Grade Count:7
Dielectric Strength 17.0 - 100 kV/mm
432 - 2540 kV/in
Average value: 33.0 kV/mm Grade Count:8
Arc Resistance 15.0 - 185 sec
15.0 - 185 sec
Average value: 103 sec Grade Count:3
Comparative Tracking Index 350 - 600 V
350 - 600 V
Average value: 493 V Grade Count:7
Processing Properties Metric English Comments
Processing Temperature 220 - 271 °C
428 - 520 °F
Average value: 240 °C Grade Count:3
Nozzle Temperature 250 - 275 °C
482 - 527 °F
Average value: 264 °C Grade Count:4
Melt Temperature 230 - 290 °C
446 - 554 °F
Average value: 257 °C Grade Count:19
Mold Temperature 40.0 - 100 °C
104 - 212 °F
Average value: 72.4 °C Grade Count:22
Drying Temperature 70.0 - 120 °C
158 - 248 °F
Average value: 83.7 °C Grade Count:18
Moisture Content 0.150 - 0.200 %
0.150 - 0.200 %
Average value: 0.192 % Grade Count:12
Injection Pressure 40.0 - 120 MPa
5800 - 17400 psi
Average value: 85.4 MPa Grade Count:6