Polymer Property : Tensile Modulus = 16.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527-2
PolyOne OnForce™ LFT PP-60LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer)
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527, ASTM D638
Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6
Description: Nilamid B3 H G10 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key characte..
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
Nilit FRIANYL A63 H-GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus 16.0 GPa

@Temperature 23.0 °C
2320 ksi

@Temperature 73.4 °F
ISO 527
Victrex® PEEK 150FW30 PEEK, 30% Carbon Fibre/PTFE Reinforced
Product Description:High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA fo..
Tensile Modulus 16.0 GPa
2320 ksi
Conditioned; ISO 527-2
Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA)  (Unverified Data**)
Ixef 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance. - Natural: Ixef..
Tensile Modulus 16.0 GPa
2320 ksi
Cookson Group Plaskon® 3100 Novolac Epoxy Molding Compound  (discontinued **)
Test specimens were transfer molded and post cured 4 hours at 175°C.A flame retardant, novolac-hardened epoxy molding compound recommended for semiconductor packages that are not stress sensitive.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
Grupo Repol Dinalon® A1S25 G50 PA66 50% Glass Fiber
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Tensile Modulus 16.0 GPa
2320 ksi
LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I..
Tensile Modulus 16.0 GPa
2320 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LCL33EXQ PEEK
LNP* LUBRICOMP* LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527-2
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha..
Tensile Modulus 16.0 GPa
2320 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WCP36 PBT (Europe-Africa-Middle East)
LNP* LUBRICOMP* WCP36 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber, PTFE, Silicone. Added features include; Internally Lubricated, Electrically Conductive.
Tensile Modulus 16.0 GPa
2320 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp RF00AES PA 66 (Europe-Africa-Middle East)
LNP THERMOCOMP* RF00AES is a compound based on PA66 resin containing Glass Fiber, Mold Release.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
dry; ISO 527-1/-2
DSM Stanyl® 46HF4550 PA46-GF50
50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
CP-Polymer-Technik Wellamid® 6000 CF 30 HWCP 30% Carbon Fiber Nylon 6, Heat Stabilized, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527-1/-2
DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry)
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Tensile Modulus 16.0 GPa
2320 ksi
dry; ISO 527-1/-2
DSM Stanyl® TW278F10 (PA46+PTFE)-GF50
50% Glass Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Modulus 16.0 GPa
2320 ksi
conditioned; ISO 527-1/-2
EMS-Grivory Grivory® HTV-45H1 black 9205 PA6T/6I-GF45
Product description: Grivory HTV-45H1 black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation a..
Tensile Modulus 16.0 GPa
2320 ksi
conditioned; ISO 527-1/-2
EMS-Grivory Grivory® GVS-5H black 9915 PA*-GF50
Product description: Grivory GVS-5H black 9915 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam..
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
Information provided by A. Schulman.
Tensile Modulus 16.0 GPa
2320 ksi
Longitudinal; ASTM D638
Sawbones Fourth-Generation Simulated Cortical Bone (Short Fiber Filled Epoxy)
Fourth-generation bones model natural cortical bone using a mixture of short glass fibers and epoxy resin pressure injected around a foam core. Standard bone models are manufactured with a solid rig..