Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 16.0 GPa | 2320 ksi | |
Plastcom SLOVAMID 66 GF 45 PA66, 45% glass fibre FeaturesChemically reinforced with 45% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. W.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | |
Plastcom SLOVAMID 66 GF 50 TS PA 66 reinforced with 50% glass fibre, thermal stability Features: Chemically reinforced with 50% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry... |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A |
Celanese VECTRA V143XL LCP, 42% Glass Reinforced
(Unverified Data**) LCP/PPS blend. Maintains most of the characteristics of E130i with improved weldline strength and flatness in certain geometries. 40% glass reinforced.LCP/PPS Blend, 40% glass reinforcedA three-zo.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
Lanxess Durethan® BKV 50 H2.0 EF DUS30 901510 Nylon 6, Glass Fiber Reinforced PA 6, 50% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | |
LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-2 |
Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater tha.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-2 |
Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA), 50% Glass Fiber (Conditioned) Ixef® 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance.Features: Go.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66 Information provided by A. Schulman. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1 |
Vyncolit Neopreg Kinel® SK4503 S5 Aramid Reinforced Molding Compound Long aramid fiber reinforced BMI molding compound suited for very demanding tribologic applications under medium to poor lubricated conditions, high temperatures & PV levelsInformation provided by S.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 90º, RT, Dry; EN2561 |
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber Information provided by HexCel |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1/-2 |
DSM Akulon® K224-G0 Nylon 6-50% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® GV-5HL black 9914 PA*-GF50 Product description: Grivory GV-5HL black 9914 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyam.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® GVS-5H nat PA*-GF50 Product description: Grivory GVS-5H natural is a 50% glass-fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyamide.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSC-30/4 LF 15 black 9832 PA666-(CF+Z)45 Product description: Grilon TSC-30/4 LF 15 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% carbon fibers and 15% of a combination of PTFE and silicone oil. Grilon .. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® HTN 53G50LWSF BK702A Polyphthalamide (PPA)
(Unverified Data**) 50% Glass Reinforced High Performance Polyamide with Low Warpage and High Stiffness Information provided by DuPont Performance Polymers |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 1 mm/min; ISO 527 |
Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded Staramide RF00AES is a 50% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 50V S3)Information provided by Eurostar. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® HT1V-45 HY black 9205 PA6T/6I-GF45 Product description: Grivory HT1V-45 HY black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-45 HY .. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
Eurotec® Tecodur® PB70 GR45 NL100 HS01 PBT/PET, 45% glass fiber reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
Eurotec® Tecopet® PT70 GR45 NL100 PR PET, 45% glass fiber reinforced, heat stabilized, natural, fast crystallization grade Information provided by Eurotec® |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | dry; ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 GF50 Polyamide 6 - Glass Fiber Reinforced 50% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A |
Celanese VECTRA V143LC LCP, 40% Specialty High Weldline strength, low warpage, 40% glass reinforced.VECTRA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommen.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
Celanese Vectra® A440 Liquid Crystal Polymer (LCP), Glass/PTFE Filled Information provided by Celanese Corporation. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 50mm/min; ISO 527-2/1A |
Celanese Celstran® PA6-GF50-01 Nylon 6, 50% Glass Reinforced 50% long strand fiber glass reinforced nylon 6 NaturalInformation provided by Celanese |
|||
Tensile Modulus | 16.0 GPa @Temperature -40.0 °C |
2320 ksi @Temperature -40.0 °F |
ASTM D638 |
Celanese Celstran® PA6-GF50-01 Nylon 6, 50% Glass Reinforced 50% long strand fiber glass reinforced nylon 6 NaturalInformation provided by Celanese |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 1mm/min; ISO 527-2/1A |
Celanese VECTRA V140 LCP, 40% Glass Reinforced LCP/PPS blend. Maintains most of the characteristics of A130 with improved weldline strength. 40% glass reinforced.VECTRA should in principle be predried. Because of the necessary low maximum resi.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | 1 mm/min; ISO 527-2/1A |
Celanese VECTRA® T130 30% Glass Filled Liquid Crystal Polymer (LCP) Description: A new 30% glass filled LCP with very high temperature capability and a UL V-0 rating at thin wall thicknesses required in today's E/E market.Information provided by Celanese Corpora.. |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1/-2 |
DuPont Performance Polymers Sorona® 2045G BK346A Polytrimethylene Terephthalate (PTT)
(Unverified Data**) 45% Glass Reinforced Polytrimethylene TerephthalateInformation provided by DuPont Performance Polymers |
|||
Tensile Modulus | 16.0 GPa | 2320 ksi | Longitudinal; ASTM D638 |
Sawbones Fourth-Generation Simulated Cortical Bone (Short Fiber Filled Epoxy) Fourth-generation bones model natural cortical bone using a mixture of short glass fibers and epoxy resin pressure injected around a foam core. Standard bone models are manufactured with a solid rig.. |