Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Nilit
Trade Name Nilamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid B3 H G10 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key characteristics: High tensile strengthHigh stiffnessEasy processingGood heat stability up to 120°CGood surface finishColorable Information provided by NILIT.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ASTM D792, ISO 1183
Water Absorption 0.80 %
0.80 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 4.5 %
4.5 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 230 MPa
33400 psi
ISO 527, ASTM D638
Elongation at Break 2.0 %
2.0 %
ISO 527, ASTM D638
Tensile Modulus 16.0 GPa
2320 ksi
ISO 527, ASTM D638
Flexural Yield Strength 300 MPa
43500 psi
ISO 178, ASTM D790
180 MPa

@Temperature 90.0 °C
26100 psi

@Temperature 194 °F
ISO 178, ASTM D790
Flexural Modulus 15.0 GPa
2180 ksi
ISO 178, ASTM D790
8.10 GPa

@Temperature 90.0 °C
1170 ksi

@Temperature 194 °F
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
17.0 kJ/m²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179
4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
ISO 179
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75, ASTM D648
Vicat Softening Point 218 °C
424 °F
49 N; ISO 306, ASTM D1525
223 °C
433 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Oxygen Index 24 %
24 %
ASTM D2863
Glow Wire Test 650 °C

@Thickness 3.20 mm
1200 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
650 °C

@Thickness 0.800 mm
1200 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
Electrical Properties Metric English Comments
Dielectric Strength 21.0 kV/mm

@Thickness 2.00 mm
533 kV/in

@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index 350 V

@Thickness 3.20 mm
350 V

@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
500 V

@Thickness 3.20 mm
500 V

@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 245 - 290 °C
473 - 554 °F
Zone 1 240 - 270 °C
464 - 518 °F
hopper
Zone 2 240 - 270 °C
464 - 518 °F
Zone 3 245 - 285 °C
473 - 545 °F
Zone 4 245 - 290 °C
473 - 554 °F
Melt Temperature 245 - 280 °C
473 - 536 °F
Do not melt above 310°C
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Flammability Rating B43
FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 MPa