Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 9.00 - 13.0 MPa | 1310 - 1890 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 8502 BLK The fogging test value is 90% according to ASTM SAE-J275. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 8802 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 9103 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | >= 9.00 MPa | >= 1310 psi | ASTM D412 |
Multibase Multi-Flex® TPE G 7455 S BLK The burn rate is 0 in/min (0 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Multibase Multi-Flex® TPE G 7821 Multi-Flex® high heat compounds are a new generations elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Kraton G technology and featur.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6509 Multi-Flex® A-6509 thermoplastic elastomer blend is designed to provide processors with cost effective compounds with excellent tear strength, tensile strength and high elongation. Multi-Flex® A-.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | |
Reliance Industries METABOLIX PHO Information provided by Reliance Industries |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1390P Polyethylene
(discontinued **) Low-density polyethylene 1390P is used primarily in extrusion-coating applications that require fast line speeds and relatively low coating weights. When compared with other low-density polyethylen.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 811A Polyethylene
(discontinued **) Injection grade. With its high melt index, the material flows well in molding machines and fills large molds with ease. It is used for molding housewares and other items where a flexible, easy mol.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
Eastman 811P Polyethylene
(discontinued **) Injection grade. With its high melt index, the material flows well in molding machines and fills large molds with ease. It is used for molding housewares and other items where a flexible, easy mol.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
ExxonMobil Escorene® LD-402 LDPE Electrical Jacketing Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A low density polyethylene homopolymer resin designed for high speed extrusions. |
|||
Tensile Strength, Ultimate | 9.00 - 80.0 MPa | 1310 - 11600 psi | Average value: 30.1 MPa Grade Count:177 |
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 9.00 - 161.337 MPa @Temperature -40.0 - 120 °C |
1310 - 23400.0 psi @Temperature -40.0 - 248 °F |
Average value: 69.4 MPa Grade Count:3 |
Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D412 |
DuPont Performance Polymers Kalrez® 1058 FFKM Perfluoroelastomer
(discontinued **) A carbon black-filled compound that has been plasticized with perfluorinated oil. It is the softest, lowest modulus compound in the Kalrez line. Generally it is similar in resistance to Compound 1.. |
|||
Tensile Strength, Ultimate | 9.00 MPa @Temperature 49.0 °C |
1310 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | |
ATG s.r.l. EACM Ethylene-Acrylic Rubber |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2035 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Medium flow resin with good stiffness.Applications: Injection molding: color concentrates.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under c.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2051 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very good molding processability, produces parts with good stiffness, and shows excellent flatness in large projected areas. Also recommended for multi-cavit.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2072 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, gloss, and stiffness.Applications: Injection molding: lids and difficult to fill applications... |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
Huntsman PE2075 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: .. |
|||
Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | Average value: 11.4 MPa Grade Count:28 |
Overview of materials for Low Density Polyethylene (LDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Extrusion Grade". Each property range of values reported is minimum and.. |
|||
Tensile Strength, Ultimate | 9.00 - 15.0 MPa | 1310 - 2180 psi | Average value: 12.3 MPa Grade Count:3 |
Overview of materials for Very Low Density Polyethylene (VLDPE) This property data is a summary of similar materials in the MatWeb database for the category "Very Low Density Polyethylene (VLDPE)". Each property range of values reported is minimum and maximum va.. |
|||
Tensile Strength, Ultimate | 9.00 - 25.0 MPa | 1310 - 3630 psi | Average value: 13.0 MPa Grade Count:20 |
Overview of materials for Low Density Polyethylene (LDPE), Wire/Cable Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Wire/Cable Grade". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 9.00 - 62.0 MPa | 1310 - 8990 psi | Average value: 41.4 MPa Grade Count:56 |
Overview of materials for Polyether Block Amide (PEBA) This property data is a summary of similar materials in the MatWeb database for the category "Polyether Block Amide (PEBA)". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 9.00 - 50.9 MPa | 1310 - 7380 psi | Average value: 34.0 MPa Grade Count:3 |
Overview of materials for ABS/PVC Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 250 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 9.00 - 60.0 MPa @Temperature 60.0 - 120 °C |
1310 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |
|||
Tensile Strength, Ultimate | 9.00 - 140.653 MPa @Temperature -40.0 - 120 °C |
1310 - 20400.0 psi @Temperature -40.0 - 248 °F |
Average value: 58.0 MPa Grade Count:30 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Tensile Strength, Ultimate | 9.00 - 15.0 MPa @Temperature 60.0 - 90.0 °C |
1310 - 2180 psi @Temperature 140 - 194 °F |
Average value: 12.0 MPa Grade Count:1 |
Overview of materials for Polypropylene Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Copolymer". Each property range of values reported is minimum and maximum values of approp.. |