Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Glass fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.940 - 1.53 g/cc
0.0340 - 0.0553 lb/in³
Average value: 1.16 g/cc Grade Count:60
Filler Content 10.0 - 50.0 %
10.0 - 50.0 %
Average value: 25.7 % Grade Count:14
Water Absorption 0.0100 - 0.300 %
0.0100 - 0.300 %
Average value: 0.0768 % Grade Count:37
Linear Mold Shrinkage 0.00100 - 0.0350 cm/cm
0.00100 - 0.0350 in/in
Average value: 0.00705 cm/cm Grade Count:50
Linear Mold Shrinkage, Transverse 0.00800 - 0.00900 cm/cm
0.00800 - 0.00900 in/in
Average value: 0.00833 cm/cm Grade Count:3
Melt Flow 0.200 - 10.0 g/10 min
0.200 - 10.0 g/10 min
Average value: 3.72 g/10 min Grade Count:14
Ash 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 24.0 % Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell R 50.0 - 112
50.0 - 112
Average value: 74.3 Grade Count:36
Tensile Strength, Ultimate 11.0 - 113 MPa
1600 - 16400 psi
Average value: 48.7 MPa Grade Count:32
9.00 - 161.337 MPa

@Temperature -40.0 - 120 °C
1310 - 23400.0 psi

@Temperature -40.0 - 248 °F
Average value: 69.4 MPa Grade Count:3
Tensile Strength, Yield 19.0 - 82.7 MPa
2760 - 12000 psi
Average value: 46.0 MPa Grade Count:35
Elongation at Break 1.00 - 290 %
1.00 - 290 %
Average value: 14.6 % Grade Count:51
Elongation at Yield 2.00 - 10.0 %
2.00 - 10.0 %
Average value: 4.23 % Grade Count:7
Modulus of Elasticity 0.700 - 13.6 GPa
102 - 1970 ksi
Average value: 4.94 GPa Grade Count:33
7.17055 - 15.2374 GPa

@Temperature -40.0 - 93.3 °C
1040.02 - 2210.03 ksi

@Temperature -40.0 - 200 °F
Average value: 11.2 GPa Grade Count:2
Flexural Yield Strength 17.2 - 186 MPa
2500 - 27000 psi
Average value: 71.9 MPa Grade Count:52
61.3633 - 215.116 MPa

@Temperature -40.0 - 93.3 °C
8900.02 - 31200.1 psi

@Temperature -40.0 - 200 °F
Average value: 138 MPa Grade Count:2
Flexural Modulus 0.965 - 11.7 GPa
140 - 1700 ksi
Average value: 4.13 GPa Grade Count:61
1.40 - 14.0653 GPa

@Temperature -40.0 - 120 °C
203 - 2040.03 ksi

@Temperature -40.0 - 248 °F
Average value: 6.70 GPa Grade Count:3
Compressive Yield Strength 9.50 - 55.2 MPa
1380 - 8000 psi
Average value: 26.8 MPa Grade Count:7
Izod Impact, Notched 0.267 - 3.74 J/cm
0.500 - 7.00 ft-lb/in
Average value: 1.14 J/cm Grade Count:57
2.1356 - 4.59154 J/cm

@Temperature -40.0 - 93.3 °C
4.0009 - 8.60184 ft-lb/in

@Temperature -40.0 - 200 °F
Average value: 3.36 J/cm Grade Count:2
Izod Impact, Unnotched 1.17 - 13.3 J/cm
2.20 - 25.0 ft-lb/in
Average value: 5.86 J/cm Grade Count:31
Izod Impact, Notched (ISO) 5.00 - 11.0 kJ/m²
2.38 - 5.23 ft-lb/in²
Average value: 7.67 kJ/m² Grade Count:3
Izod Impact, Unnotched (ISO) 25.0 - 35.0 kJ/m²
11.9 - 16.7 ft-lb/in²
Average value: 31.7 kJ/m² Grade Count:3
Charpy Impact Unnotched 1.70 - 2.00 J/cm²
8.09 - 9.52 ft-lb/in²
Average value: 1.83 J/cm² Grade Count:3
Charpy Impact, Notched 2.40 - 10.0 J/cm²
11.4 - 47.6 ft-lb/in²
Average value: 4.60 J/cm² Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 19.8 - 180 µm/m-°C
11.0 - 100 µin/in-°F
Average value: 68.4 µm/m-°C Grade Count:29
Thermal Conductivity 0.288 - 0.400 W/m-K
2.00 - 2.78 BTU-in/hr-ft²-°F
Average value: 0.336 W/m-K Grade Count:7
Deflection Temperature at 0.46 MPa (66 psi) 72.2 - 143 °C
162 - 290 °F
Average value: 123 °C Grade Count:42
Deflection Temperature at 1.8 MPa (264 psi) 51.7 - 127 °C
125 - 260 °F
Average value: 108 °C Grade Count:48
Vicat Softening Point 80.0 - 92.0 °C
176 - 198 °F
Average value: 86.3 °C Grade Count:4
Flammability, UL94 HB
HB
Grade Count:35
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+16 ohm-cm
1000 - 1.00e+16 ohm-cm
Average value: 6.64e+15 ohm-cm Grade Count:22
Surface Resistance 1e+05 - 1.00e+13 ohm
1e+05 - 1.00e+13 ohm
Average value: 3.33e+12 ohm Grade Count:3
Dielectric Constant 2.30 - 2.80
2.30 - 2.80
Average value: 2.65 Grade Count:6
Dielectric Strength 11.8 - 45.0 kV/mm
300 - 1140 kV/in
Average value: 19.3 kV/mm Grade Count:15
Dissipation Factor 0.00400 - 0.00800
0.00400 - 0.00800
Average value: 0.00667 Grade Count:6
Arc Resistance 140 - 180 sec
140 - 180 sec
Average value: 147 sec Grade Count:6
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 40.0 - 227 °C
104 - 440 °F
Average value: 183 °C Grade Count:23
Die Temperature 230 - 240 °C
446 - 464 °F
Average value: 235 °C Grade Count:3
Melt Temperature 170 - 249 °C
338 - 480 °F
Average value: 217 °C Grade Count:11
Mold Temperature 21.1 - 180 °C
70.0 - 356 °F
Average value: 49.2 °C Grade Count:29
Drying Temperature 70.0 - 100 °C
158 - 212 °F
Average value: 83.4 °C Grade Count:10
Moisture Content 0.200 %
0.200 %
Average value: 0.200 % Grade Count:3
Injection Pressure 4.96 - 124 MPa
720 - 18000 psi
Average value: 80.4 MPa Grade Count:22