Polymer Property : Tensile Strength, Ultimate = 16700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO value at 5mm/min.
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Tensile Strength, Ultimate	115 - 115 MPa @Temperature 125 - 125 °C	16700 - 16700 psi @Temperature 257 - 257 °F	Average value: 115 MPa Grade Count:1
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO 527
LATI LAPEX A G/20 20% Glass Fiber Reinforced Polyethersulfone (PES) (UL94 V-0) (Unverified Data**) Description: Lapex A compounds are polyethersulfone (PES) products. They are high temperature compounds offering an interesting combination of properties. Lapex A provides outstanding thermal resist..
Tensile Strength, Ultimate	115 - 180 MPa @Time 180000 - 7.20e+7 sec	16700 - 26100 psi @Time 50.0 - 20000 hour	Average value: 139 MPa Grade Count:4
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E..
Tensile Strength, Ultimate	115 MPa	16700 psi	ASTM D638
Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound (discontinued **) Black Polyphenylene Sulfide CompoundRyton® R10-110BL is a glass and mineral filled polyphenylene sulfide compound which provides a good combination of mechanical and electrical properties.Applicati..
Tensile Strength, Ultimate	115 MPa @Temperature 980 Â°C	16700 psi @Temperature 1800 Â°F
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	115 MPa	16700 psi	ASTM D638
Tipco Tipcolite® VASW 200 Phenolic Compound, Long Glass Fiber, in fluffy form, Medium -Soft Flow & Very High Strength
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO 527-93
Wellman Wellpet® MRGF102-BK1 PET, 35% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division.
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO 527-1/-2
DSM Arnite® B427 SE/R PBT-GF35 FR(17) 35% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO 527-1/-2
DSM Arnite® TV4 244 S PBT-GF20 FR 20% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	115 MPa	16700 psi	cond; ISO 527-1/-2
DSM EcoPaXX® Q-KG6 PA410-GF30 % Glass Reinforced, Heat Stabilized, for E&E applications
Tensile Strength, Ultimate	115 MPa	16700 psi	cond; ISO 527-1/-2
DSM Stanyl® 46HF4530 PA46-GF30 30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Strength, Ultimate	115 MPa @Temperature 160 °C	16700 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications
Tensile Strength, Ultimate	115 MPa @Temperature 160 °C	16700 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate	115 MPa	16700 psi	cond; ISO 527-1/-2
DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate	115 MPa	16700 psi	5 mm/min
Arkema Group Rilsan® BZM 30 TL Nylon 11, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA11,MHL,18-050,GF30Rigid grade with glass fiber (30%) filler for injection molding. Available colors: black and natural. Light and heat stabilized.Rigidity. High compressive st..
Tensile Strength, Ultimate	115 MPa	16700 psi	5mm/min; ISO 527
BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The com..
Tensile Strength, Ultimate	115 MPa	16700 psi	5 mm/min
Arkema Group Rilsan® AZM 30 O TLD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-050,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: natural. Light and heat stabilizing agent. Mold-release agent.High rigidity. High..
Tensile Strength, Ultimate	115 MPa	16700 psi	5mm/min; ISO 527
BASF Ultradur B 4300 G4 LS High Speed BK15045 20% Glass Filled PBT
Tensile Strength, Ultimate	115 MPa	16700 psi	5mm/min; ISO 527
BASF Ultramid® B3EG3 BK00564 15% Glass Filled PA6 (Dry) Ultramid B3EG3 BK00564 is a 15% glass fiber reinforced, pigmented black injection molding PA6 grade for housings with enhanced impact resistance.
Tensile Strength, Ultimate	115 - 115 MPa @Temperature -40.0 - -40.0 °C	16700 - 16700 psi @Temperature -40.0 - -40.0 °F	Average value: 115 MPa Grade Count:1
Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced". Each property range of values repo..
Tensile Strength, Ultimate	115 MPa	16700 psi	ASTM data at 5 mm/min.
BASF Capron® GR30 20% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR30 is a 30% glass reinforced polyamide 6 injection molding compound. IT is also available in heat stabilized (Capron GR30 HS) and/or pigmented versions. The glass fiber reinforcement enhanc..
Tensile Strength, Ultimate	115 MPa	16700 psi	ASTM data at 5 mm/min.
BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR30 HS is a heat stabilized 30% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest..
Tensile Strength, Ultimate	115 MPa	16700 psi	ISO 527
LATI LAESTRA G/40-V0CT1 40% Glass Fiber Reinforced, Elastomer Modified, Flame Retardant Syndiotactic Polystyrene (SPS) Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270..
Tensile Strength, Ultimate	115 MPa	16700 psi	5mm/min; ISO 527
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in..