Polymer Property : Tensile Strength, Ultimate = 4060 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638-61T
Rotuba 860S Ethyl Cellulose Data provided by the manufacturer.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PP 1375 PRE-ELEC PP 1375 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PP 1383 PRE-ELEC PP 1383 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638
North Wood Plastics PS with 60% Wood Fiber Data provided by North Wood Plastics, Inc.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM Data
Americas Styrenics Styron® XL-8023VC High Impact Polystyrene (discontinued **) STYRON® XL-8023 VC high impact polystyrene is designed to provide molders of VCR cassettes with the impact and gloss they require, at economics and processability highly advantaged over ABS resins...
Tensile Strength, Ultimate	28.0 MPa	4060 psi	DIN 53455
Ineos Nova S-4200 Medium Impact Compact Polystyrene (discontinued **) Medium impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection molding of technical..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	DIN 53455
Ineos Nova S-7600MG Compact Polystyrene Microgranulates (discontinued **) High impact polystyrene Microgranulates, having a diameter of 0.8 -1.0 mm, especially useful for compounding and extrusion applications. Due to the very high viscosity and the absence of weakener, ..
Tensile Strength, Ultimate	28.0 - 46.0 MPa @Temperature 60.0 - 90.0 °C	4060 - 6670 psi @Temperature 140 - 194 °F	Average value: 37.0 MPa Grade Count:1
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638
NOVA Chemicals Novapol® HB-Y556-A HDPE Extrusion Resin (discontinued **) Molded Plaque Properties. Features: Excellent ESCR, high rigidity and impact strength, good melt strength.Applications: chemical bottles, toys, blend for use with post-consumer resins.Data provided..
Tensile Strength, Ultimate	28.0 MPa @Thickness 1.60 mm	4060 psi @Thickness 0.0630 in	Sintered moldings; ASTM D4894/4895
3M Dyneon™ TF 2024 PTFE Paste Extrusion Powder (discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 500. Average particle size 500µm. Used for unsintered tapes and sealing cords.Dyneon offers a family of PTFE fine powder ..
Tensile Strength, Ultimate	28.0 MPa @Thickness 1.60 mm	4060 psi @Thickness 0.0630 in	Sintered moldings; ASTM D4894/4895
3M Dyneon™ TF 2025 PTFE Paste Extrusion Powder (discontinued **) Type I PTFE. Free flowing powder. Minimum reduction ratio is 20; Max is 300. Average particle size 500µm. Used for liners.Dyneon offers a family of PTFE fine powder paste extrusion resins. Thes..
Tensile Strength, Ultimate	28.0 - 116 MPa @Temperature -40.0 - 80.0 °C	4060 - 16800 psi @Temperature -40.0 - 176 °F	Average value: 73.0 MPa Grade Count:2
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	Compounded Tire
Natural Rubber, Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber..
Tensile Strength, Ultimate	28.0 MPa	4060 psi
Kuraray HYBRARÂ® PH8 Polypropylene Blend Description: HYBRARÂ® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRARÂ® is a special thermoplastic rubb..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	at max load; ISO 527
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	28.0 MPa @Temperature 80.0 °C	4060 psi @Temperature 176 °F	ASTM D638
Toyobo T-661 Nylon 66, Standard Grade (Conditioned) Features: Non-reinforced, Standard GradeInformation provided by Toyobo.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	at max load; ISO 527
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	at max load; ISO 527
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	DIN 53504
Lubrizol ESTANE® 58300 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	DIN 53504
Lubrizol ESTANE® 58866 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ISO 37
Lubrizol ESTANE® GP65AE Ester Based Thermoplastic Polyurethane Type: Estane® GP 65AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	at max load; ISO 527
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	at max load; ISO 527
A. Schulman FORMION™ FI 397 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638/D412
Covestro Bayflex® 180 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System 0.1 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and offi..
Tensile Strength, Ultimate	>= 28.0 MPa	>= 4060 psi	DIN 53 504
Dow BETAMATE™ 7000/7050 L Epoxy Two component room temperature fast curing polyurethane structural adhesive with high elastic modulus.Information provided by Dow
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638/D412
Covestro Bayflex® XGT-100 Polyurethane Elastomeric RIM, 15% Milled Glass Filled, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D638
A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Tensile Strength, Ultimate	28.0 - 203 MPa	4060 - 29500 psi	Average value: 140 MPa Grade Count:477
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Tensile Strength, Ultimate	28.0 MPa	4060 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)& Gum compound with 100 parts Hypalon; 4 parts high activity magnesia; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont Dow Elastomers). Reinforcing fillers not needed..