- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 158 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 158 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Mytex Polymers AN16L-53 Polypropylene, Compounded Description: Compounded polypropylene produced for automotive exterior applications using Mytex® Technology.Key Applications: Body side moldingInformation provided by Mytex Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PET 1451 PRE-ELEC PET 1451 is a conductive thermoplastic compound based on PETG. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PET 14.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PP 1383 PRE-ELEC PP 1383 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75/2Bf |
| Radici Radilon® CS38FL (dry) Copolyamide 6 semiaromatic Film gradeInformation provided by Radici group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75 |
| Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 89.0 °C | 158 - 192 °F | Average value: 74.0 °C Grade Count:18 |
| Overview of materials for PCTG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PCTG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| LATI LASTIROL R-V0 Polystyrene (PS) (UL94 V-0)
(discontinued **) Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass fiber reinforc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Chevron Phillips HiD® 9075 HDPE Injection Molding Resin
(discontinued **) Resin Type: linear copolymer; ASTM D3350 Classification 335540A; ASTM D4976 Classification: PE 235, A 54607Characteristics: excellent flow, moderate impact strength, good stiffness, moderate ESCR, e.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| LyondellBasell Lupolen® 4261 A HDPE, Blow Molding Grade Easy-to-process bow molding grade for technical containers such as fuel tanks, petrol filler inlets, expansion tanks, horticultural spray tanks, tanks for lawnmowers, disposable containers (up to 10.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Hyosung Topilene C600H PP C600H Film Grade Butane Random CopolymerApplications: Sealable CPP/OPPCharacteristics:Very low sealSlip propertyTransparencyInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C @Thickness 6.40 mm |
158 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical KEYFLEX BT HB9255D Ester Type TPE Description: TPC-ET, Blow Moldable, Medium Modulus, Black ColorApplication: Air duct, Hose & TubingCAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Ineos B50-35H-176 HDPE B50-35H is a high density polyethylene copolymer developed for blow molding. It is recommended for use in applications which require a combination of high top load strength and good environmental s.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Borealis Borecene Compact™ RM8346RC Black Linear Polyethylene for Rotational Molding Borecene Compact RM8346RC is a third generation linear medium density black polyethylene for rotational molding. Borecene RM8346RC is a special grade, which has passed rigorous tests and can be con.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Borealis Bormed™ RD804CF Polypropylene Random Copolymer Bormed™ RD804CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications Bormed™ RD804CF is recommended for packaging for med.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Borealis Borstar® HE3410 HDPE for Sewage Pipes Borstar® HE3410 is a bimodal polyethylene compound produced by the advanced Borstar® technology. Well dispersed carbon black gives outstanding UV resistance. Long term stability is ensured by an .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Borealis Daplen™ KSR4525 Polypropylene Reactor Elastomer Modified Daplen KSR4525 is a reactor elastomer modified polypropylene intended for injection molding. Daplean KSR4525 is a material with excellent impact/stiffness ratio. The grade is available in natural .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Cadence™ GS1 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Drystar 0113 Copolyester This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Eastar MN211 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. MN211 contains a mold release.Application.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Eastman Eastman 1223 Copolyester Applications:Blown filmCredit cardsDebit cardsDeodorant packagingElectronic packagingFabricated boxesFlexible packagingFood packagingFurniture/Furniture trimGaming cardsGift cardsIdentification card.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75-2/B |
| ExxonMobil HDPE HMA 025 High Density Polyethylene Resin Product Description: HMA 025 is a HDPE grade, characterized by excellent dimensional stability, impact strength and very high stiffness. Availability: Africa & Middle East, Asia Pacific and Europe A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO-R 75 Method B |
| Hippe PE 1000 Polyethylene Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | Annealed; ASTM Data |
| Engineered Plastics EPABS 54 ABS Injection Grade Pellets. GMP # 002. Property values below represent typical values. Information provided by Engineered Plastics Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow UNIVAL™ DMDD-6200 NT 7 High Density Polyethylene Resin (HDPE) Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6200 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package hous.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM-D648 |
| Braskem GM7746C HDPE Blow Molding Polyethylene GM7746C is a high-density polyethylene specially developed for the manufacturing of blow molding fuel tanks. It has high molar mass and excellent mechanical properties. It also shows excellent tenac.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D-648 |
| Axiall SP-7008 Rigid PVC, Molding Georgia Gulf SP-7008 is a rigid vinyl compound formulated for electrical fittings and molded parts requiring high impact strength and toughness.Information provided by Georgia GulfGeorgia Gulf becam.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Carmel Olefins CAPILENE® TR 50 Polypropylene Impact Copolymer Description: CAPILENE® TR 50 is a medium melt flow rate heterophasic copolymer with very high impact strength, even at low temperature, designed for injection molding. This grade combines good pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Braskem Green PE SGM7746C Blow Molding and Monofilament High Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Mono.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Ineos HB111R Polyethylene Copolymer HB111R is a natural high molecular weight, high-density copolymer polyethylene developed for automotive fuel tanks. It combines excellent processability and outstanding physical performance, particu.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 - 96.1 °C | 158 - 205 °F | Average value: 84.7 °C Grade Count:17 |
| Overview of materials for Polystyrene, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Flame Retardant". Each property range of values reported is minimum and maximum values of a.. |
|||