Overview of materials for Nylon 66, MoS2 Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, MoS2 Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.08 - 1.45 g/cc
0.0390 - 0.0524 lb/in³
Average value: 1.18 g/cc Grade Count:43
Water Absorption 0.300 - 8.50 %
0.300 - 8.50 %
Average value: 1.37 % Grade Count:18
Moisture Absorption at Equilibrium 2.60 - 2.80 %
2.60 - 2.80 %
Average value: 2.73 % Grade Count:3
Water Absorption at Saturation 7.00 - 8.50 %
7.00 - 8.50 %
Average value: 8.00 % Grade Count:5
Linear Mold Shrinkage 0.00300 - 0.0210 cm/cm
0.00300 - 0.0210 in/in
Average value: 0.0131 cm/cm Grade Count:39
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113 - 120
113 - 120
Average value: 117 Grade Count:16
Tensile Strength, Ultimate 48.3 - 145 MPa
7000 - 21000 psi
Average value: 84.8 MPa Grade Count:33
Tensile Strength, Yield 46.0 - 145 MPa
6670 - 21000 psi
Average value: 90.2 MPa Grade Count:18
Elongation at Break 3.50 - 70.0 %
3.50 - 70.0 %
Average value: 14.4 % Grade Count:33
Elongation at Yield 4.00 - 100 %
4.00 - 100 %
Average value: 38.3 % Grade Count:4
Modulus of Elasticity 2.41 - 4.14 GPa
350 - 600 ksi
Average value: 3.58 GPa Grade Count:17
Flexural Yield Strength 11.7 - 228 MPa
1700 - 33000 psi
Average value: 118 MPa Grade Count:39
Flexural Modulus 1.69 - 8.27 GPa
245 - 1200 ksi
Average value: 3.45 GPa Grade Count:43
Compressive Yield Strength 34.5 - 110 MPa
5000 - 16000 psi
Average value: 85.0 MPa Grade Count:3
Izod Impact, Notched 0.267 - 7.88 J/cm
0.500 - 14.8 ft-lb/in
Average value: 0.764 J/cm Grade Count:42
Izod Impact, Unnotched 4.32 - 18.7 J/cm
8.09 - 35.0 ft-lb/in
Average value: 10.6 J/cm Grade Count:15
Izod Impact, Notched (ISO) 5.00 - 5.00 kJ/m²

@Temperature -30.0 - -30.0 °C
2.38 - 2.38 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.00 kJ/m² Grade Count:1
Izod Impact, Unnotched (ISO) NB - NB

@Temperature -30.0 - -30.0 °C
NB - NB

@Temperature -22.0 - -22.0 °F
Grade Count:1
Coefficient of Friction 0.200 - 0.270
0.200 - 0.270
Average value: 0.240 Grade Count:3
K (wear) Factor 70.0 - 302 x 10-8 mm³/N-M
34.7 - 150 x 10-10 in³-min/ft-lb-hr
Average value: 184 x 10<sup>-8</sup> mm³/N-M Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 64.8 - 81.0 µm/m-°C
36.0 - 45.0 µin/in-°F
Average value: 71.6 µm/m-°C Grade Count:5
Thermal Conductivity 0.245 - 0.259 W/m-K
1.70 - 1.80 BTU-in/hr-ft²-°F
Average value: 0.252 W/m-K Grade Count:4
Melting Point 249 - 275 °C
480 - 527 °F
Average value: 257 °C Grade Count:12
Maximum Service Temperature, Air 80.0 - 200 °C
176 - 392 °F
Average value: 128 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 195 - 254 °C
383 - 490 °F
Average value: 224 °C Grade Count:27
Deflection Temperature at 1.8 MPa (264 psi) 64.0 - 248 °C
147 - 478 °F
Average value: 99.6 °C Grade Count:41
Flammability, UL94 HB - V-2
HB - V-2
Grade Count:23
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 - 1.00e+16 ohm-cm
1.00e+13 - 1.00e+16 ohm-cm
Average value: 2.09e+15 ohm-cm Grade Count:16
Surface Resistance 1.00e+13 - 1.00e+14 ohm
1.00e+13 - 1.00e+14 ohm
Average value: 2.80e+13 ohm Grade Count:5
Dielectric Constant 3.60 - 3.80
3.60 - 3.80
Average value: 3.68 Grade Count:5
Dielectric Strength 13.8 - 120 kV/mm
350 - 3050 kV/in
Average value: 50.9 kV/mm Grade Count:6
Dissipation Factor 0.0150 - 0.0200
0.0150 - 0.0200
Average value: 0.0167 Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 270 - 293 °C
518 - 560 °F
Average value: 285 °C Grade Count:9
Melt Temperature 260 - 304 °C
500 - 580 °F
Average value: 281 °C Grade Count:21
Mold Temperature 40.0 - 110 °C
104 - 230 °F
Average value: 81.4 °C Grade Count:27
Drying Temperature 73.9 - 100 °C
165 - 212 °F
Average value: 80.6 °C Grade Count:16
Moisture Content 0.200 %
0.200 %
Average value: 0.200 % Grade Count:8
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:7
Injection Pressure 4.96 - 124 MPa
720 - 18000 psi
Average value: 66.1 MPa Grade Count:17