3M Scotch-Weld™ 1751 B/A Epoxy Adhesive
| Category | Polymer , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | 3M |
| Trade Name | Scotch-Weld™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Scotch-Weld™ 1751 B/A Epoxy Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive 1751 B/A is a gray, aluminum filled, two-part, room temperature curing structural adhesive.Information provided by 3M
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 - 80 | 75 - 80 | ASTM D2240 |
| Shear Strength | 4.76 MPa | 690 psi | Overlap, Maple to Polyester |
| 13.8 MPa | 2000 psi | Overlap, Al/Al, Hyd Oil 30 days @ RT; ASTM D1002-72 | |
| 13.8 MPa | 2000 psi | Overlap, Al/Al, Tap Water 30 days @ RT; ASTM D1002-72 | |
| 13.8 MPa | 2000 psi | Overlap, Al/Al, 20% Salt Spray 30 days @ 35°C; ASTM D1002-72 | |
| 14.9 MPa | 2160 psi | Overlap, Steel to Aluminum | |
| 15.2 MPa | 2200 psi | Overlap, Al/Al, 149°C Aged 8 days; ASTM D1002-72 | |
| 15.48 MPa | 2245 psi | Overlap, Steel to Copper | |
| 16.8 MPa | 2440 psi | Overlap, Steel to Steel | |
| 17.7 MPa | 2570 psi | Overlap, Aluminum to Copper | |
| 138 MPa | 20000 psi | Overlap, Al/Al, JP-4 Fuel 30 days @ RT; ASTM D1002-72 | |
| 1.38 MPa @Temperature 82.0 °C |
200 psi @Temperature 180 °F |
Overlap, Steel Solvent Wipe; ASTM D1002-72 | |
| 3.45 MPa @Temperature 82.0 °C |
500 psi @Temperature 180 °F |
Overlap, Aluminum FPL Etch; ASTM D1002-72 | |
| 9.65 MPa @Temperature -55.0 °C |
1400 psi @Temperature -67.0 °F |
Overlap, Aluminum FPL Etch; ASTM D1002-72 | |
| 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Overlap, Steel Solvent Wipe; ASTM D1002-72 | |
| 13.8 MPa @Temperature 24.0 °C |
2000 psi @Temperature 75.2 °F |
Overlap, Aluminum FPL Etch; ASTM D1002-72 | |
| 16.5 MPa @Temperature 24.0 °C |
2400 psi @Temperature 75.2 °F |
Overlap, Steel Solvent Wipe; ASTM D1002-72 | |
| Peel Strength | 0.701 kN/m | 4.00 pli | T-Peel, Aluminum FPL Etch; ASTM D1876-61T |
| 0.877 kN/m | 5.00 pli | T-Peel, Steel Solvent Wipe; ASTM D1876-61T |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.385 W/m-K | 2.67 BTU-in/hr-ft²-°F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 480 - 720 min | 8.00 - 12.0 hour | Time to Handling Strength |
| 10100 min | 168 hour | Full | |
| Shelf Life | 24.0 Month | 24.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Amber | Accelerator |
| Gray | Base | |
| Gray |
Users viewing this material also viewed the following:
- Unifrax Fiberfrax® LDS Moldable Moldable Insulation
- Zhejiang Juner PC-A7-7 Top-Grade Flame Retardant UV-Resistant
- Dow Corning SILASTIC® E RTV SILICONE RUBBER KIT
- Eurostar Staramide PF006ES PA6, 30% Glass Fiber Filled, Injection Molded
- Dow Nordel® IP 4570 Dense Extruded Profile
- Arlon LW301C##FR-P1 0.030" (0.762 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Americas Styrenics STYRON A-TECH® 1400AS High Impact Polystyrene
- Arlon 99202R008 0.008" (0.203 mm) Cured Silicone Rubber with PTFE Coated Fiberglass Carrier
- 3M FM00G Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Quadrant EPP Duratron® PAI T4301 Polyamide-imide, extruded bearing grade (ASTM Product Data Sheet)
Copyright © lookpolymers.com All Rights Reserved