3M Scotch-Weld™ 2214 Non-Metallic Filled Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ 2214 Non-Metallic Filled Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Non-Metallic Filled is a non-metal filled version of Scotch-Weld adhesive 2214 regular. One part 250°F (121°C) curing 100% solids, 3M™ Scotch-Weld™ Epoxy Adhesive 2214 is a paste consistency epoxy adhesive designed for bonding metals and many high temperature plastics such as fiberglass reinforced plastic, polyester, and phenolicsInformation provided by 3M
Physical Properties Metric English Comments
Viscosity 50 - 200 cP
50 - 200 cP
Mechanical Properties Metric English Comments
Hardness, Shore D >= 85
>= 85
Tensile Strength, Ultimate 62.1 MPa
9000 psi
Elongation at Break <= 2.0 %
<= 2.0 %
Modulus of Elasticity 4.83 GPa
700 ksi
Shear Strength 2.07 MPa

@Temperature -53.0 °C
300 psi

@Temperature -63.4 °F
Aluminum Overlap
2.76 MPa

@Temperature 177 °C
400 psi

@Temperature 351 °F
Aluminum Overlap
4.14 MPa

@Temperature 149 °C
600 psi

@Temperature 300 °F
Aluminum Overlap
10.3 MPa

@Temperature 121 °C
1500 psi

@Temperature 250 °F
Aluminum Overlap
27.6 MPa

@Temperature 24.0 °C
4000 psi

@Temperature 75.2 °F
Aluminum Overlap
31.0 MPa

@Temperature 82.0 °C
4500 psi

@Temperature 180 °F
Aluminum Overlap
Thermal Properties Metric English Comments
CTE, linear 130 µm/m-°C

@Temperature -30.0 - 100 °C
72.2 µin/in-°F

@Temperature -22.0 - 212 °F
Thermal Conductivity 0.209 W/m-K
1.45 BTU-in/hr-ft²-°F
Electrical Properties Metric English Comments
Volume Resistivity 2.50e+13 ohm-cm
2.50e+13 ohm-cm
Dielectric Strength 22.4 kV/mm

@Thickness 0.991 mm
570 kV/in

@Thickness 0.0390 in
Arc Resistance 26 sec
26 sec
Descriptive Properties Value Comments
Appearance Cream