Polymer Property : Tensile Strength, Ultimate = 9000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Nylene® 9110 Unfilled Nylon 6/10 Description: Nylene® 9110 is an unfilled specialty nylon. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation...
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Nylene® Naxel™ PC1210 Polycarbonate Description: Naxel™ PC1210 is a 6 melt, general purpose polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Nylene® Naxel™ PC43 UV Resistant Polycarbonate Description: Naxel™ PC43 is a medium flow, UV resistant polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Nylene® Naxel™ PC45G FR 10% Glass Reinforced, Flame Retardant Polycarbonate Description: Naxel™ PC45G FR is a 10% glass fiber reinforced, flame retardant polycarbonate. PC45G FR is UL approved. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins ar..
Tensile Strength, Ultimate	62.1 - 150 MPa	9000 - 21800 psi	Average value: 102 MPa Grade Count:7
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp..
Tensile Strength, Ultimate	62.05 MPa	9000 psi
Abatron AboCast 8-2/Abocure 8-2 Epoxy (discontinued **) 2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 100 g (3.5 oz.): 265 minutes; cures in 3 weeks at 25°C (77°F).Applications: solventless casting, adh..
Tensile Strength, Ultimate	62.05 MPa	9000 psi
Abatron AboCast 8-13/Abocure 8-13 Epoxy (discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 53 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Global PC-1424 Standard Grade Polycarbonate Information provided by Global Polymers Corporation.
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Techmer ES ElectrafilÂ® DB-50/SS/6/FR Polycarbonate, 6% Stainless Steel Fiber (dry blend), Flame Retardant
Tensile Strength, Ultimate	62 MPa	9000 psi	ASTM D638
Sumitomo Bakelite DurezÂ® 152 Phenolic, Injection Grade Durez 152 Phenolic is a two-stage, heat resistant/electrical molding material. It exhibits superior dimensional stability, good strength retention at elevated temperature and good molded appearance..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Lubrizol ISOPLAST™ 202EZ Engineering Thermoplastic Polyurethane Resin NSF Standard 61 CertifiedAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009.
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D412
Lubrizol Estane® AG 9550 Thermoplastic Polyurethane Type: Estane® AG 9550 is a polyether based aliphatic polyurethane designed for flat die extrusion into film and sheet products.Features: Very tough, high modulus, high tear and tensile properties t..
Tensile Strength, Ultimate	62.1 MPa @Temperature 760 °C	9000 psi @Temperature 1400 °F
Crucible Steel 416 Plus Chromium Steel Crucible 416 Plus is a hardenable chromium steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of standard AISI Type 4..
Tensile Strength, Ultimate	62.05 MPa	9000 psi
Abatron AboCast/AboCure 8109-4 Safety hardener (minimum toxicity) version of 8109-3.Processing: 100/10 pbw; Potlife: 2.5 h/20°C (68°F), 30 min/40°C (105°F), 15 min/60°C (140°F); mix at RT; cures in: 24 h/20°C (68°F), 2-3 ..
Tensile Strength, Ultimate	62.1 MPa	9000 psi
AdvanSource Biomaterials ChronoFlex® AL 65D Biodurable Medical Grade Polyurethane ChronoFlex® AL is a family of premium polycarbonate aliphatic biodurable thermoplastic polyurethane elastomers developed by AdvanSource Biomaterials Corporation. ChronoFlex® AL medical-grade elas..
Tensile Strength, Ultimate	62.1 - 82.7 MPa	9000 - 12000 psi
Bulk Molding Compounds BMC 685 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 685 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, oil ..
Tensile Strength, Ultimate	62.1 - 75.8 MPa	9000 - 11000 psi
Bulk Molding Compounds BMC 840 Corrosion Resistant Molding Compound BMC 840 is a very high strength, corrosion resistant compound suitable for compression, transfer and stuffer injection molding.Typical applications are pump housings and impellers.
Tensile Strength, Ultimate	62.1 - 82.7 MPa	9000 - 12000 psi
Bulk Molding Compounds BMC 695 Vinyl Ester Molding Compound BMC 695 vinyl ester molding compound is a mineral filled glass fiber-reinforced vinyl ester compound suitable for compression and injection molding It is characterized by good moldability, oil and s..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Nylene® Naxel™ PC41 Polycarbonate Description: Naxel™ PC41 is a 12 melt, general purpose polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources ..
Tensile Strength, Ultimate	62.1 - 228 MPa	9000 - 33000 psi	Average value: 161 MPa Grade Count:37
Overview of materials for Nylon 66, Glass Fiber/MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/MoS2 Filled". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	62.1 MPa	9000 psi	Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Stat-Tech™ AS-30GF/000 SD Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **) Description/Features:Glass Fiber ReinforcedAntistaticInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate	62.1 - 115 MPa	9000 - 16700 psi	Average value: 96.0 MPa Grade Count:12
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc..