ATI Allegheny Ludlum 316Ti Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel , T S30000 Series Stainless Steel
Manufacturer ATI Allegheny Ludlum
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Allegheny Ludlum 316Ti Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:excellent resistance to general corrosion, excellent resistance to pitting/crevice corrosion, resistant to sensitization, better creep stress-rupture and tensile strength at elevated temperatures then Type 304. Information provided by Allegheny Ludlum
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 76
76
Tensile Strength, Ultimate 620 MPa
89900 psi
78.0 MPa

@Temperature 982 °C
11300 psi

@Temperature 1800 °F
155 MPa

@Temperature 871 °C
22500 psi

@Temperature 1600 °F
261 MPa

@Temperature 760 °C
37900 psi

@Temperature 1400 °F
375 MPa

@Temperature 649 °C
54400 psi

@Temperature 1200 °F
423 MPa

@Temperature 538 °C
61400 psi

@Temperature 1000 °F
433 MPa

@Temperature 427 °C
62800 psi

@Temperature 801 °F
443 MPa

@Temperature 316 °C
64300 psi

@Temperature 601 °F
455 MPa

@Temperature 204 °C
66000 psi

@Temperature 399 °F
518 MPa

@Temperature 93.0 °C
75100 psi

@Temperature 199 °F
Tensile Strength, Yield 55.0 MPa

@Temperature 982 °C
7980 psi

@Temperature 1800 °F
112 MPa

@Temperature 871 °C
16200 psi

@Temperature 1600 °F
145 MPa

@Temperature 538 °C
21000 psi

@Temperature 1000 °F
146 MPa

@Temperature 649 °C
21200 psi

@Temperature 1200 °F
146 MPa

@Temperature 760 °C
21200 psi

@Temperature 1400 °F
146 MPa

@Temperature 427 °C
21200 psi

@Temperature 801 °F
159 MPa

@Temperature 316 °C
23100 psi

@Temperature 601 °F
179 MPa

@Temperature 204 °C
26000 psi

@Temperature 399 °F
208 MPa

@Temperature 93.0 °C
30200 psi

@Temperature 199 °F
248 MPa

@Strain 0.200 %
36000 psi

@Strain 0.200 %
Elongation at Break 54 %
54 %
in 2"
19.5 %

@Temperature 649 °C
19.5 %

@Temperature 1200 °F
23 %

@Temperature 760 °C
23 %

@Temperature 1400 °F
23 %

@Temperature 538 °C
23 %

@Temperature 1000 °F
25 %

@Temperature 427 °C
25 %

@Temperature 801 °F
26 %

@Temperature 316 °C
26 %

@Temperature 601 °F
28 %

@Temperature 204 °C
28 %

@Temperature 399 °F
39.5 %

@Temperature 93.0 °C
39.5 %

@Temperature 199 °F
41 %

@Temperature 982 °C
41 %

@Temperature 1800 °F
48 %

@Temperature 871 °C
48 %

@Temperature 1600 °F
Thermal Properties Metric English Comments
CTE, linear 16.5 µm/m-°C

@Temperature 20.0 - 100 °C
9.17 µin/in-°F

@Temperature 68.0 - 212 °F
18.2 µm/m-°C

@Temperature 20.0 - 500 °C
10.1 µin/in-°F

@Temperature 68.0 - 932 °F
19.5 µm/m-°C

@Temperature 20.0 - 1000 °C
10.8 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 14.6 W/m-K

@Temperature 100 °C
101 BTU-in/hr-ft²-°F

@Temperature 212 °F
Melting Point 1345 - 1440 °C
2453 - 2620 °F
Solidus 1345 °C
2453 °F
Liquidus 1440 °C
2620 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.080 %
<= 0.080 %
Chromium, Cr 16 - 18 %
16 - 18 %
Iron, Fe >= 61.295 %
>= 61.295 %
As Remainder
Manganese, Mn <= 2.0 %
<= 2.0 %
Molybdenum, Mo 2.0 - 3.0 %
2.0 - 3.0 %
Nickel, Ni 10 - 14 %
10 - 14 %
Nitrogen, N <= 0.10 %
<= 0.10 %
Phosphorous, P <= 0.045 %
<= 0.045 %
Silicon, Si <= 0.75 %
<= 0.75 %
Sulfur, S <= 0.030 %
<= 0.030 %
Titanium, Ti <= 0.70 %
<= 0.70 %