- Adamas Adalon® 266 PTFE, Mineral/Glass Bubbles Filler
Adamas Adalon® 266 PTFE, Mineral/Glass Bubbles Filler
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 266 PTFE, Mineral/Glass Bubbles Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 - 1.70 g/cc | 1.65 - 1.70 g/cc | ASTM D792 |
| Deformation | 1.8 - 2.2 % | 1.8 - 2.2 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 13.4 - 16.8 % | 13.4 - 16.8 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 50 - 54 | 50 - 54 | ASTM D2240 |
| Ball Indentation Hardness | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 13.0 MPa | >= 1890 psi | ASTM D4894 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D4894 |
| Compressive Strength | >= 22.0 MPa @Temperature 23.0 °C, Time 86400 sec |
>= 3190 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 230 °C | 446 °F | DSC |
| Minimum Service Temperature, Air | -80.0 °C | -112 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF50 - PA6 Nylon 6, 50% Long Glass Fiber Reinforced
- SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS
- LG Chemical Lupox® TE5000G PBT+PC
- Momentive Performance Materials Siloprenâ„¢ LSR 2651 Liquid Silicone Rubber - Non Post Cure / Low Compression Set
- Momentive Performance Materials Silplusâ„¢ 80 MP Heat Cured Rubber
- DAK Americas Laser+® W P45A PET
- Diamond Polymers DIAMALOY 761 ABS/PC Alloy, Non-Halogen Flame Retardant with 5% PTFE
- Arkema Group Orgalloy® RS 6620 Nylon 66 Alloy, 20% Glass Fiber (Conditioned)
- Beijing Ranger Chem PBT-201-G10 291 Flame Retarding FR PBT
- 3M FM05540K MC Polyester Label Product
Copyright © lookpolymers.com All Rights Reserved