Advanced Elastomer Systems Santoprene® 101-64 W175 Thermoplastic Rubber  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Elastomer Systems Santoprene® 101-64 W175 Thermoplastic Rubber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A black thermoplastic general purpose elastomer designed for thin wall extrusion with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfonated polyethylene. It can be processed using extrusion or other melt processing techniques.Key Features: Flame resistance HB rating; Designed for thin wall extrusion applications; Continuous temperature rating 1000 hrs. @ 135°C (275°F); Excellent flex fatigue resistance; Excellent ozone resistanceAdditional processing comments: This thermoplastic rubber is a shear-dependent material that can be processed on conventional thermoplastic equipment for injection molding, extrusion, or blow molding. For extrusion, a general purpose screw with a compression ratio of 2.5 to 3.0 is recommended. Material can be recycled. SANTOPRENE rubber is incompatible with acetal and PVC.Values below are for injection molded plaques, side gated, 82.6 mm x 117.5 mm x 3.0 mm. Tensile properties measured across flow. Data provided by Advanced Elastomer Systems.Advanced Elastomer Systems is now a part of ExxonMobil. This grade was removed from the Advanced Elastomers Systems standard product line before the ExxonMobil acquisiton.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
TPE-0105 (ASTM D792)
Mechanical Properties Metric English Comments
Hardness, Shore A 64
64
5 Second; TPE-0169 (ASTM D 2240)
Tensile Strength, Ultimate 6.90 MPa
1000 psi
TPE-0153 (ASTM D 412)
Elongation at Break 400 %
400 %
TPE-0153 (ASTM D 412)
100% Modulus 0.00230 GPa
0.334 ksi
TPE-0153 (ASTM D 412)
Graves Tear Strength 10.2 kN/m

@Temperature 100 °C
58.2 pli

@Temperature 212 °F
TPE-0056 (ASTM D 624)
24.5 kN/m

@Temperature 23.0 °C
140 pli

@Temperature 73.4 °F
TPE-0056 (ASTM D 624)
Compression Set 23 %
23 %
23°C, 168 hrs.; TPE-0016 (ASTM D 412)
36 %

@Temperature 100 °C
36 %

@Temperature 212 °F
168 hrs.; TPE-0016 (ASTM D 412)
Tensile Set 10 %
10 %
23°C, 168 hrs.; TPE-0053 (ASTM D 412)
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Continuous temperature Rating, 1000 hours
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
TPE-0089 (ASTM D 746)
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Processing Temperature 177 - 232 °C
351 - 450 °F
Drying Temperature 82.0 °C
180 °F
Desiccant drying for 3 hours recommended
Dry Time 3 hour
3 hour