Arlon 25662T010 0.010" (0.254 mm) Cured Silicone Rubber with Laminated ETFE Film Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 25662T010 0.010" (0.254 mm) Cured Silicone Rubber with Laminated ETFE Film Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Cured Silicone RubberSubstrate: Laminated ETFE FilmChemical Compatibility: (ETFE offers good chemical resistance to the following classes of chemicals) Alkalis, Organic and Inorganic acids, Amines, Epoxies, Aromatic compounds, Chlorine compounds, Ethers, Ketones, Esters, Alcohols and HydrocarbonsProduct Use: Chemically resistant, reusable vacuum bag materialAppearance: Translucent silicone rubber chemically bonded to fluoropolymer filmThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	Silicone; Arlon SQA-TMS-024
	1.70 g/cc	0.0614 lb/in³	Laminated ETFE Film; ASTM D792
Thickness	50.8 microns	2.00 mil	Substrate; Arlon SQA-TMS-003
	203 microns	8.00 mil	Side 1; Arlon SQA-TMS-003
	254 microns	10.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55	55	Silicone; ASTM D2240
	67	67	Laminated ETFE Film; ASTM D2240
Tensile Strength	8.96 MPa	1300 psi	Silicone; ASTM D412
	41.4 MPa	6000 psi	Laminated ETFE Film; ASTM D638
Elongation at Break	300 %	300 %	Laminated ETFE Film; ASTM D638
	700 %	700 %	Silicone; ASTM D412
Elongation at Yield	6 % @Temperature 20.0 °C	6 % @Temperature 68.0 °F	Elastic Deformation of ETFE Film; ASTM D638
Tear Strength	39.4 kN/m	225 pli	Arlon SQA-TMS-029
	1.58 kN/m @Temperature 150 °C	9.00 pli @Temperature 302 °F	[ppiw], Break Strength; Arlon SQA-TMS-008
	2.28 kN/m @Temperature 100 °C	13.0 pli @Temperature 212 °F	[ppiw], Break Strength; Arlon SQA-TMS-008
	4.03 kN/m @Temperature 20.0 °C	23.0 pli @Temperature 68.0 °F	[ppiw], Break Strength; Arlon SQA-TMS-008

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	154 °C	310 °F
Minimum Service Temperature, Air	-51.1 °C	-60.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	7.87 kV/mm	200 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Shelf Life	60.0 Month @Temperature 21.1 - 26.7 °C	60.0 Month @Temperature 70.0 - 80.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Translucent
Total Product Weight (oz/yd2)	9.6	Arlon SQA-TMS-025