Arlon 47573R007 0.0075" (0.190 mm) Cured Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 47573R007 0.0075" (0.190 mm) Cured Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Cured RubberSide 2: Cured Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness >= 50.8 microns
>= 2.00 mil
Side 1
>= 50.8 microns
>= 2.00 mil
Side 2
76.2 microns
3.00 mil
Polyethylene Interleave
88.9 microns
3.50 mil
Prime Coated 2113 Fiberglass, Substrate
165 - 216 microns
6.50 - 8.50 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 40 - 50
40 - 50
Compound Property
Tensile Strength >= 5.52 MPa
>= 800 psi
Compound Property
Elongation at Break >= 500 %
>= 500 %
Compound Property
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
UL RTI, Electrical 200 °C
392 °F
per UL Card E54153
UL RTI, Mechanical without Impact 220 °C
428 °F
per UL Card E54153
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 12.0 Month

@Temperature 21.1 °C
12.0 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 7.7 - 9.5
Uncoated Fabric Break Strength 195 lb/in
Warp Direction, Substrate Property
75 lb/in
Fill Direction, Substrate Property
Copyright © lookpolymers.com All Rights Reserved