Azoty Tarnow™ TARNOFORM 300 GF6 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 300 GF6 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
ISO 62
Linear Mold Shrinkage 0.0102 cm/cm

@Thickness 4.00 mm
0.0102 in/in

@Thickness 0.157 in
Melt Flow 4.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 200 MPa
29000 psi
358 N; ISO 2039-1
Tensile Strength at Break 120 MPa
17400 psi
ISO 527
Elongation at Break 3.5 %
3.5 %
ISO 527
Tensile Modulus 9.30 GPa
1350 ksi
ISO 527
Flexural Strength 176 MPa
25500 psi
ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.570 J/cm²
2.71 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Specific Heat Capacity 1.21 J/g-°C
0.289 BTU/lb-°F
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 163 °C
325 °F
ISO 75
Vicat Softening Point 162 °C
324 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.2

@Frequency 100 Hz
4.2

@Frequency 100 Hz
IEC 60250
4.2

@Frequency 1e+6 Hz
4.2

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.0095

@Frequency 1e+6 Hz
0.0095

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F