BASF Luranyl® KR 2402 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene
Manufacturer	BASF
Trade Name	Luranyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Luranyl® KR 2402 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Base grade with a balanced combination of impact strength and stiffness for parts calling for good heat deformation resistance (e.g. warm-air vents, coil formers, sheet and wheel covers).Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English
Density	1.06 g/cc	0.0383 lb/in³
Water Absorption	0.30 %	0.30 %
Moisture Absorption at Equilibrium	0.10 %	0.10 %
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in
High Load Melt Index	30 g/10 min @Load 21.6 kg, Temperature 250 °C	30 g/10 min @Load 47.6 lb, Temperature 482 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	64.0 MPa	9280 psi
Elongation at Break	35 %	35 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	2.50 GPa	363 ksi
Charpy Impact Unnotched	NB	NB
	4.00 J/cm² @Temperature -30.0 °C	19.0 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	2.50 J/cm²	11.9 ft-lb/in²
	2.50 J/cm² @Temperature -30.0 °C	11.9 ft-lb/in² @Temperature -22.0 °F
Tensile Creep Modulus, 1 hour	2300 MPa	334000 psi
Tensile Creep Modulus, 1000 hours	1900 MPa	276000 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 20.0 °C	36.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	133 °C	271 °F
Deflection Temperature at 1.8 MPa (264 psi)	119 °C	246 °F
Vicat Softening Point	136 °C	277 °F
Flammability, UL94	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in
Oxygen Index	22 %	22 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.5 @Frequency 1e+6 Hz	2.5 @Frequency 1e+6 Hz
	2.6 @Frequency 100 Hz	2.6 @Frequency 100 Hz
Dielectric Strength	95.0 kV/mm	2410 kV/in
Dissipation Factor	0.00050 @Frequency 1e+6 Hz	0.00050 @Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V