BASF Ultramid® 8202 PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8202 PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ultramid 8202 HS) and/or pigmented versions. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance.
Physical Properties Metric English Comments
Density 0.932 g/cc
0.0337 lb/in³
Melt; ISO 1183
1.13 g/cc
0.0408 lb/in³
dry; ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.5 %
9.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.7 %
2.7 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 48
48
Formic Acid
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
0.2 in/min; ASTM Test
80.0 MPa

@Temperature -40.0 °C
11600 psi

@Temperature -40.0 °F
ASTM Test
80.0 MPa

@Temperature -40.0 °C
11600 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Yield 36.0 MPa
5220 psi
2 in/min; ASTM Test
36.0 MPa
5220 psi
50mm/min; ISO 527
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ISO Data
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ASTM Test
30.0 MPa

@Temperature 80.0 °C
4350 psi

@Temperature 176 °F
ASTM Test
30.0 MPa

@Temperature 80.0 °C
4350 psi

@Temperature 176 °F
ISO Data
110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
ASTM Test
110 MPa

@Temperature -40.0 °C
16000 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
2 in/min; ASTM Test
2.5 %

@Temperature -40.0 °C
2.5 %

@Temperature -40.0 °F
ASTM Test
2.5 %

@Temperature -40.0 °C
2.5 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 16 %
16 %
50mm/min; ISO 527
16 %
16 %
2 in/min; ASTM Test
35 %

@Temperature 80.0 °C
35 %

@Temperature 176 °F
ASTM Test
35 %

@Temperature 80.0 °C
35 %

@Temperature 176 °F
ISO Data
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ASTM Test
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ISO Data
Tensile Modulus 0.970 GPa
141 ksi
1mm/min; ISO 527
0.320 GPa

@Temperature 120 °C
46.4 ksi

@Temperature 248 °F
ISO Data
0.550 GPa

@Temperature 80.0 °C
79.8 ksi

@Temperature 176 °F
ISO Data
4.00 GPa

@Temperature -40.0 °C
580 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 25.0 MPa
3630 psi
ISO Data
35.0 MPa
5080 psi
ASTM Test
154 MPa

@Temperature -40.0 °C
22300 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 0.740 GPa
107 ksi
ASTM Test
0.770 GPa
112 ksi
ISO Data
Izod Impact, Notched 0.430 J/cm

@Temperature -40.0 °C
0.806 ft-lb/in

@Temperature -40.0 °F
ASTM Test
NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
Specific Heat Capacity 3.728 J/g-°C
0.8910 BTU/lb-°F
Melt
Thermal Conductivity 0.264 W/m-K
1.83 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding
Mold Temperature 80.0 °C
176 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
UL.UL-C Yes