BNZ Materials Bazelite 2000 Insulating Castable

Category Ceramic , Oxide , Silicon Oxide
Manufacturer BNZ Materials, Inc.
Trade Name Bazelite
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BNZ Materials Bazelite 2000 Insulating Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BNZ manufactures a variety of insulating and dense castable refractories to meet the exacting needs of the high temperature processing industries. These hydraulic setting products are suitable for installation by various methods including gunning, casting or slap-troweling. Each product is specifically formulated to economically obtain the desired properties for the application and service temperature for which it is intended.Information provided by BNZ Materials Inc.
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0370 lb/in³
Fired at 5 hrs at 816°C
Mechanical Properties Metric English Comments
Modulus of Rupture 0.000460 GPa

@Temperature 540 °C
0.0667 ksi

@Temperature 1000 °F
Fired; ASTM C258
0.000620 GPa

@Temperature 815 °C
0.0899 ksi

@Temperature 1500 °F
ASTM C258
0.000620 GPa

@Temperature 1095 °C
0.0899 ksi

@Temperature 2003 °F
ASTM C258
0.00103 GPa

@Temperature 104 °C
0.149 ksi

@Temperature 219 °F
Dried; ASTM C258
Compressive Strength 2.34 MPa

@Temperature 1095 °C
340 psi

@Temperature 2003 °F
2.90 MPa

@Temperature 815 °C
420 psi

@Temperature 1500 °F
2.96 MPa

@Treatment Temp. 540 °C
430 psi

@Treatment Temp. 1000 °F
Cold Crush Strength; Fired at 540°C
4.14 MPa

@Treatment Temp. 104 °C
600 psi

@Treatment Temp. 219 °F
Cold Crush Strength; Dried 104°C
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1149 °C
2100 °F
Shrinkage 0.10 %

@Temperature 540 °C
0.10 %

@Temperature 1000 °F
Permanent Linear Change; ASTM C210
0.20 %

@Temperature 815 °C
0.20 %

@Temperature 1500 °F
Permanent Linear Change; ASTM C210
0.30 %

@Temperature 1095 °C
0.30 %

@Temperature 2003 °F
Permanent Linear Change; ASTM C210
Component Elements Properties Metric English Comments
Al2O3 34 %
34 %
CaO 15.8 %
15.8 %
Fe2O3 6.5 %
6.5 %
MgO 0.30 %
0.30 %
Na2O 0.80 %
0.80 %
Includes K<sub>2</sub>O
SiO2 40.1 %
40.1 %
TiO2 1.9 %
1.9 %