Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer Beijing Chemical Industry Research Institute (Group)
Trade Name KAIFA®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group)
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.0 MPa
12900 psi
ASTM D638
Flexural Strength 150 MPa
21800 psi
ASTM D790
Izod Impact, Notched 0.800 J/cm

@Thickness 3.20 mm
 1.50 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Charpy Impact Unnotched 3.60 J/cm²
17.1 ft-lb/in²
ISO179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
ASTM D648
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Strength 23.0 kV/mm

@Thickness 2.00 mm
 584 kV/in

@Thickness 0.0787 in
 ASTM D149
Processing Properties Metric English Comments
Rear Barrel Temperature 210 - 220 °C
410 - 428 °F
Middle Barrel Temperature 235 - 245 °C
455 - 473 °F
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Nozzle Temperature 240 - 245 °C
464 - 473 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 130 °C
266 °F
Dry Time 4 hour
4 hour
Injection Pressure 80.0 - 120 MPa
11600 - 17400 psi